Steel 44Х2НМБР (АБО70В)

Designation

Name The value
Designation GOST Cyrillic 44Х2НМБР
Designation GOST Latin 44X2HMBP
Transliteration 44H2NMBR
By chemical elements 44Cr2НMoNbB
Name The value
Designation GOST Cyrillic АБО70В
Designation GOST Latin ABO70B
Transliteration ABO70V
By chemical elements -

Description

44Х2НМБР steel is used: for the manufacture of rolled plates for the production of various parts of power plant engineering.

Standards

Name Code Standards
Blanks. Of the workpiece. Slabs В31 TU 14-1-2012-77
Sheets and strips В33 TU 14-1-2538-78

Chemical composition

Standard C S P Mn Cr Si Ni Fe B Mo Nb
TU 14-1-2012-77 0.44-0.48 ≤0.012 ≤0.012 0.6-0.9 1.8-2.2 0.4-0.6 0.8-1.2 Rest 0.001-0.003 0.35-0.6 0.01-0.03
Fe is the basis.
According to TU 14-1-2012-77 the chemical composition is given for steel 44Х2НМБР-ВД (АБО70В-ВД). Boron is introduced by calculation and chemical analysis is not determined. Deviations in chemical composition - in accordance with GOST 4543, except sulfur, phosphorus and manganese. Deviations in sulfur and phosphorus are allowed, provided that their total content does not exceed 0.020%. Deviations in the content of manganese should be within the range of +0.10 / -0.15%. The residual content of tungsten should not exceed 0.30%. The residual copper content should not exceed 0.25%. A technological addition of vanadium in an amount up to 0.15% is allowed.

Mechanical properties

Section, mm σU, MPa d5, % KCU, kJ/m2
Slabs on the other 14-1-2012-77. Quenching in oil or in air from 950±10 °C + Vacation at 220±10 °C (2-4 h exposure). Allowed prior normalization of the samples
≥1860 ≥7 ≥196

Description mechanical marks

Name Description
σU Limit short-term strength
d5 Elongation after rupture
KCU Toughness

Technological properties

Name The value
Macrostructure and pollution On the other 14-1-2012-77 in the macrostructure of steel slabs are allowed: - point nonuniformity ≤ 2 points; - the Central porosity ≤ 1 score; - square of exudation ≤ 1 points; layer-by-layer crystallization of ≤ 3 points. Pollution steel non-metallic inclusions should be: - sulphides ≤ 1.5 points; - oxides of stroke ≤ 1.5 points; - the fragile silicates ≤ 1.5 points; - the silicates plastic ≤ 1.5 points; - the nitrides of all kinds ≤ 2.0 points. Allowed attacks to 2 points no more than 2 samples of the sulphides, oxides, stroke, silicates fragile and plastic. Allowed attacks to 3 points with no more than two samples of the nitrides of all kinds, provided that in this case the sum of points of all types of inclusions does not exceed 5.
Particularities of production of goods Slabs on the other 14-1-2012-77 are supplied in heat-treated (annealing or high tempering) without measuring hardness.