The company Evek GmbH offers a bargain price to purchase bulk metal products of stainless steel AISI 436 (1.4113). You can buy the profile at a bargain price from the manufacturer, with timely delivery of products to any region specified by the customer.

Composition and properties

Stainless steel grade AISI 436 (1.4113) is a stainless steel of ferrite class. It contains an average amount of chromium, but is further alloyed with molybdenum. According to Euro standard EN 10088-2, the steel in question includes:

The ASTM and UNS standards differ slightly in their requirements to chemical composition of the material. Thus the carbon content is limited more strictly (up to 0.02%), and there are no nitrogen and manganese in the composition.

When rolled, steel AISI 436 (1.4113) has the following physical and mechanical properties - tensile strength, MPa - 470 ... 490, the ultimate ductility, MPa - 310 ... 355, % elongation - at least 34. After rolling the hardness of the initial bulk rolling should not exceed 76...78 N. V. Smaller values of the above indicators correspond to the conditions of hot rolling of the range.

Of the basic physical and mechanical properties of steel should be noted resistance to corrosion, which occurs in the presence of concentrated aqueous acids and alkalis. Steel is also resistant to halogen compounds - chlorides, bromides, iodides, etc. The presence of chromium and chromium nitrides stabilized with titanium makes the steel resistant to pitting corrosion up to temperatures of ^800-8500 С.

The nearest analog of steel AISI 436 (1.4113) is stainless steel 12X17M, differing only by the absence of titanium in its composition. Full European analogue is steel X6 CrMo 17-1, with a somewhat lower upper limit of molybdenum content (up to 1%).

Application

Steel AISI 436 (1.4113) is used for the production of automatic purification systems and smoke detectors of metallurgical and blast furnace equipment. Rolled sheets of this steel is effective for the manufacture of complex components, some parts of which are connected by welding methods (the presence of titanium in the composition facilitates the welding process, and minimizes the possible intercrystalline corrosion of the surface).

This steel bars and wires have good machinability. Volumetric stamping of body-of-rotation type parts is possible in the cold state. With the use of automated stamping equipment. For complex configuration of parts semi-hot forming is preferable, for which the billets are heated to 400 ... ⁴⁵⁰⁰ C. Steel is also well processed on metal-cutting equipment.

To buy bulk rolled products (pipes, rounds, wires) of AISI 436 (1.4113) steel from Evek GmbH at producer prices effectively and profitably. All products are certified, and its range can satisfy any, even a demanding customer.