Grade 3 titanium - 3.7055 - CP2 circle, bar, sheet
International Equivalent
Mark | Analogue | W. Nr. | Aisi Uns | En | Order |
---|---|---|---|---|---|
VT1-1 | Delivery from the stock, in stock |
Supplier
We offer to buy circles, bars, sheets Grade 3, CP2 (titanium - 3.7055) from specialized warehouses of the supplier Evek GmbH with delivery in any city. Full compliance with international quality standards. The supplier Evek GmbH offers to buy rounds, bars, sheets Grade 3, CP2 (titanium - 3.7055), the price is optimal in the given segment of rolled products.
Technical characteristics
This grade is high-purity technical titanium that is used for the production of chemical and pharmaceutical equipment, alloying of alloys, for the needs of transport engineering. Specific gravity is 4.505 g/cm3. Brinell hardness HB 10-1 131 - 163 N/mm2. Weldability: Not restricted.
Percentage composition
Ti | Fe | C | Si | N | O | H | Impurities |
---|---|---|---|---|---|---|---|
99,038-99,7 | ≤ 0,25 | ≤ 0,08 | ≤ 0,12 | ≤ 0,05 | ≤ 0,15 | ≤ 0,012 | ≤ 0,3 |
Its melting point is 1668 °C.
Cold working
Turning, milling, grinding, drilling.
Heat treatment
Normalization, hardening, annealing, tempering.
Mechanical properties (t° 20°C).
Range | s in | sT | d5 | y |
---|---|---|---|---|
MPa | MPa | % | % | |
Sheets | 450-600 | 380-500 | 25 | 50 |
Physical properties
t° | E 10- 5 | a 10 6 | l | C |
---|---|---|---|---|
Degree | MPa | 1/Gradus | W/(m-degree) | J/(kg-degree) |
20 | 1.12 | 18.85 | 540 | |
100 | 8.2 |
sB - Ultimate short-term strength
sT - limit of proportionality (yield stress for permanent deformation)
d5 - Tensile strain at break
HB - Brinell hardness
E - Modulus of elasticity of the first kind
C - specific heat capacity