Steel x - 102Cr6 - 1.2067 - Stal 52100 circle, bars, forgings
International Equivalent
| Mark | Analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| ~1.2067 | ~~52100 | 102Cr6 | Delivery from the stock, in stock |
To buy a round, rod, forgings of tool steel grades X, 102Cr6 (1.2067) or Stal 52100 at a bargain price from the manufacturer, the company offers Electrocentury-steel. The supplier shall ensure strict compliance with the range of supply and efficient transportation of products to the point specified by the user.
Chemical composition
Steel X GOST 5950 belongs to the group of the steel deep hardenability, and is made in Russia and CIS with the following composition of its constituent components:
- Carbon — …to 0.95 to 1.10%;
- Silicon — 0,15…0,35%;
- Manganese is 0.15 to 0.49…%;
- Chrome…1,30 1,65%.
In the present steel are also inevitable metallurgical impurities — sulfur and phosphorus, the amount of which in the finished product may not exceed 0,025%.
A number of well-known foreign analogues of steel x. In particular, according to the European standard DIN 17350, ISO 4957 and is 102Cr6 tool steel (1.2067), and in the U.S. such 52100 steel is produced according to the norms ASTM А295. Their himsostav approximately identical, but allow the presence of traces of molybdenum and Nickel.
The company Electrocentury-steel implements at cost-effective prices of the producer circle, rod and forgings, made of tool steel grades X, 102Cr6 (1.2067) or Stal 52100. The provider ensures full compliance with the assortment of supply and timely transportation of the ordered products at the consumer.
Properties and applications
Due to its high hardness (achieved after hardening heat treatment), and deep hardenability of steel by the aforementioned brands are used in the manufacture of dimensional cutting and measuring tools (including knives), as well as bearings. Steel X, 102Cr6 (1.2067) and 52100 are not high corrosion resistance, but respond well to hot plastic deformation.
Physico-mechanical characteristics of steels the following:
- The tensile strength after hardening, MPa — 1400…2100;
- Yield strength, MPa — 590…750;
- Elongation, percent — 11;
- Hardness after annealing HB — 225;
- Hardness after quenching HRC 63.
To buy at cost-effective prices from the producer circle, rod and forgings, made of tool steel grades X, 102Cr6 (1.2067) or Stal 52100, the company offers Electrocentury-steel. The supplier guarantees compliance with deadlines and range of delivery, transportation of products runs directly in the address set by the user.