5V titanium circle, rod, sheet

Alloy 5V

Titanium alloys are paramagnetic, wear-resistant, durable, have a number of qualities that play an important role in technical fields. The use of titanium alloys is very promising in the field of engineering, where important heat resistance, corrosion resistance in combination with a specific strength. This is also true in aviation, shipbuilding, aerospace, railway transport. Some specific structural properties of titanium are of great interest for the food and chemical industry.

Grade:	Classification:	long steel production, manufacturing of ingots, semi-finished products; manufacture of parts spec. equipment, part, aircraft engineering, instrument making.
5V	Titanium alloys	Industrial use:

The percentage composition of the alloy 5 In accordance with GOST 1−9207 -91

Si	C	Fe	Mo	Ti	N	V	O	Zr	Al	Impurities
≤0.12	0.06 — 0.14	≤0.25	0.7 — 2	88.85 — 93.24	≤0.04	1 — 1.9	≤0.13	≤0.1	4.7 — 6.3	other 0.3

Note: the substrate 5 is titanium, its content is about 88.85 — 93.24%.

The mechanical characteristics of the alloy In 5 (20°C).

Assortment	Eg.	Size
Wire according to GOST 27265−87	490−635	16−20

Physical characteristics of the alloy 5 V.

MPa	Grad	W/(m·deg)	1/Deg	J/(kg·deg)	Ohm·m	kg/m3
1.12	20	18.85	4505
100	8.2	540
E 10 — 5	T	l	a 10 6	C	R 10 9	r

Marking physical properties:

Description	Marking
Temperature obtain information about the alloy [Hail]	— T
— The modulus of elasticity of the 1st kind [MPa]	— E
— Coefficient of thermal linear expansion (at 20°C) [1/Deg]	-a
— Electrical resistivity [Ohm·m]	-R
— Specific gravity [g/cm3]	-r
— Thermal conductivity coefficient [W/(m·deg)]	-l
— Specific heat (at 20°C) [j/(kg·deg)]	-C

Marking mechanical properties:

Description	Marking
— The limit of proportionality (yield strength for permanent deformation) [MPa]	sT
— Short-term strength [MPa]	blower SB
Contraction ratio [ % ]	y
The elongation at break [ % ]	d5
— Brinell hardness number, [MPa]	HB
— Impact strength [ kJ / m2]	KCU

Weldability:

Marking	Description
limited weldability	— required pre-heating to a temperature of 100−120°C with the final heat treatment
without restrictions	— no need for pre-heating and the final heat treatment
Difficult weldability	— required pre-heating to a temperature of 200−300°C with the final heat treatment

Alloying

High-strength titanium alloys alloyed with vanadium and aluminum, and the heat resistance is achieved additives of molybdenum and aluminum. The most used titanium alloy containing molybdenum, aluminum, vanadium. Such alloys have a particularly high strength and corrosion resistance. Aluminum is the primary alloying element, it is also important for titanium alloys, such as carbon for the iron. The second most important component is the molybdenum.

Supply

In stock, LLC «Electrocentury-steel» a wide range of products from high quality titanium. Sell wholesale and retail products from brand titanium 5 V. In the technical documentation included data on chemical composition, limiting the percentage of impurities; mechanical qualities of the products. We can buy in bulk any semi-finished products for large-scale production. We also offer optimal conditions for retail customers. A high level of service and speed of service are the face of our company.

Buy at best price

Digging LLC «Electrocentury-steel» has unlimited range of titanium alloys of the highest quality. We offer alloys for special purpose at best price from warehouses in Ukraine and Russia. If you are interested in our offer, contact your nearest office. Qualified specialists will provide all necessary information regarding the products, price range, conditions of implementation. The cost of the product depends on the parameters of products and additional conditions of delivery.