VT20-1 SV titanium welding wire
International Equivalent
| Mark | Analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| ВТ20-1 | Delivery from the stock, in stock |
Relevance
Titanium welding wire brand VT20−1sv, implemented by LLC «Electrovek-steel», meets the most stringent national and foreign standards. Popularity of the wire due to high quality, diversified product mix, the optimum value.
| alloy Brand: | Classification: | Industrial use: |
|---|---|---|
| VT20−1 St. | Titanium wrought alloys | production of welding wire |
St. VT20−1 according to GOST percentage composition of alloy 27, 265−87
| Si | C | Fe | Mo | Ti | N | V | O | Zr | H | Al | Impurities |
|---|---|---|---|---|---|---|---|---|---|---|---|
| ≤0.1 | ≤0.05 | ≤0.15 | 0.5 — 1.5 | 91.36 — 95.7 | ≤0.04 | 0.5 — 1.5 | ≤0.12 | 12 | ≤0.003 | 2 — 3 | other 0.3 |
Note: The basis of the alloy 5 is titanium, the content of about 91.36 — 95.7%.
Mechanical properties of titanium wire VT20−1 St. (Temperature 20 ° C).
| assortment | The size | Eg. |
|---|---|---|
| Titanium welding wire, GOST 27 265−87 | 12 | 590−785 |
The physical characteristics of the alloy VT20−1 St.
| W / (m · deg) | 1 / Grad | MPa | hail | kg / m3 | Ohm m | J / (kg · °) |
|---|---|---|---|---|---|---|
| 8.2 | 1.12 | 20 | 4505 | |||
| l | a June 10 | 100 | 540 | |||
| 18.85 | E 10- 5 | T | r | R September 10 | C |
Marking the physical properties:
| Description | designation |
|---|---|
| — Temperature data acquisition of the alloy [Castle] | — T |
| — Modulus of elasticity of the 1st kind, [MPa] | — E |
| — Coefficient of linear thermal expansion (at 20 ° C) [1 / deg] | -a |
| — The electrical resistance [ohm · m] | -R |
| — Specific weight [g / cm3] | -r |
| — Thermal conductivity [W / (m · deg)] | -l |
| — Specific heat capacity (at 20 ° C) [J / (kg · deg)] | -C |
Marking the mechanical properties:
| Description | designation |
|---|---|
| — The limit of proportionality (the yield strength for the residual strain) [MPa] | sT |
| — Short-term strength [MPa] | sre |
| — Reduction [%] | y |
| — Elongation at break [%] | d5 |
| — Brinell hardness in [MPa] | HB |
| — Impact strength [kJ / m2] | KCU |
| designation | Description |
|---|---|
| limited weldability | — Needs to preheating t ° 100−120 ° C with a final heat treatment |
| no limits | — No need for preliminary heating and final heat treatment |
| difficult to weld | — Needs to preheating t ° 200−300 ° C with a final heat treatment |
Basic properties
Titanium welding wire produced in degassed and etching condition. Its roundness must not exceed tolerances. Its surface must be clean and bright, with no shades of tint, neprotravov or dark spots. Traces broaches, small risks, sunsets deeper than shown in the table.
| The diameter of the wire VT20−1 St. | The wire brand VT20−1 St. depth of the defect must be no more than |
|---|---|
| 1.0 | - |
| 1.2 | - |
| 1.4 | - |
| 1.6 | - |
| 1.8 | - |
| 2.0 | 0.4 |
| 2.5 | 0.5 |
| 3.0 | 0.5 |
| 3.5 | 0.6 |
| 4.0 | 0.6 |
| 5.0 | 0.7 |
| 6.0 | 0.8 |
| 7.0 | 0.8 |
Note. On the possibility of a separate surface defects with a diameter of the wire up to 3 mm — 0.1 mm. When Ø> 3 mm — 0.2 mm. During metallographic control Macrosection amount in excess of the depth of defects shall not exceed 10%. Correct defects or surface contaminants by etching the etching is allowed to separate bays with repeated degassing.
Supply
Wire comes bays with outer diameter up to 900 mm. This wire must not be stuck together turns or bends of more than 100 °. Curl the wire after annealing, is not considered marriage. Coil weight — 50 kg. If the bay is made up of several parts, the length of each of them must not be less than 10 m.
Bay tightly ligated soft titanium wire in three places and packed in clean paper, wrapped burlap, synthetic cloth or plastic film, thickness according to GOST 10 354−82 100 — 200 microns without paper packaging. Packaged Bay ligated string of regulatory documents, respectively.
The mechanical characteristics of wire must conform to the requirements specified in the table.
| Brand Titanium Alloy | Ultimate b MPa (kgf \ mm sq.) | The wire diameter in mm | Elongation b,% not less |
|---|---|---|---|
| VT20−1sv | from 2.0 to 7.0 incl. | 645−845 (60−80) | 12.0 |
Marking:
Each bay has a fixed label indicating:
the conditional designation of the wire;
-naimenovaniya manufacturer and trademark:
-Rooms party and smelting;
-day release;
-kleyma technical control;
-oboznacheniya this standard.
Marking:
The label indicates the bay:
— Brand wire;
— The manufacturer and its trademark:
— № smelting and parties;
— date of manufacture;
— Designation of GOST.
— The availability of those. control;
Buy at a bargain price
All products of LLC «Electrovek-steel» has a very high quality. We sell wholesale, retail of titanium products at the best prices. Quality guaranteed by strict observance of production standards. Technological capabilities of each stage make it possible to carry out individual orders in the absence of the desired product in the base case. We are able to produce quality products customized non-standard parameters as soon as possible. We are waiting for your orders.