St-08H20N9G7T - 1.4370 pipe, wire, round
International Equivalent
| Mark | Analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| 12Х17Г9АН4 | EI878 | 1.4373 | 202 | X12CrMnNiN18-9-5 | Delivery from the stock, in stock |
Welding wire Sv-08H20N9G7T
This wire is produced in accordance with GOST 2246−70, RD 03−613−03 and specifications 1220−005−84 823 540−2010. It is used for manual arc welding of critical parts of structures of steel austenitic grades: 12X18H9T, 08X18H10T, 08H18N12B and similar.
It is also used for sealing internal components that operate at high pressure and temperature of 570−650 °, and for welding of steels such as marks, if the welding seam is not imposed strict requirements of resistance to intergranular corrosion.
The percentage of
| Cu | P | S | V | N | Al | W |
|---|---|---|---|---|---|---|
| Not more than 0,25 | Not more than 0,035 | No more than 0,018 | In fact | In fact | In fact | In fact |
| Mn | Si | FROM | Cr | Ti | Mo | Ni |
|---|---|---|---|---|---|---|
| 5,00−8,00 | 0,50−1,00 | Not more than 0.10 | 18,50−22,00 | 0,60−0,90 | Not more than 0,25 | 8,00−10,00 |
Mechanical properties of the wire Sv-08H20N9G7T:
Tensile strength high-alloy and alloy wire in accordance with the rules.
| The diameter of the wire, mm | for the manufacture of electrodes | for welding (welding) |
|---|---|---|
| 1.6 | 686−980 (70−100) | 882−1274 (90−130) |
| 0.8−1.5 | - | 882−1323 (90−135) |
| St. 2.0 | 637−931 (65−95) | 686−1029 (70−105) |
| 2.0 | 686−980 (70−100) | 784−1176 (80−120) |
Tolerances and wire diameters in accordance with the above:
| rated diameter | In the manufacture of electrodes | for welding (welding) |
|---|---|---|
| 1.6; 2.0 | - | -0.12 |
| 0.8 | -0.06 | -0.07 |
| 2.5; 3.0 | -0.09 | -0.12 |
| 1.2 | - | -0.09 |
| 1 | - | |
| 1.5 | -0.09 | |
| 1.4 | ||
| 4.0; 5.0; 6.0 | -0.12 | -0.16 |
Ferrite:
The composition in the wire of the ferrite phase is regulated only by agreement of the parties.
The chemical properties of the weld metal:
| Cu | P | S | V | N | Al | W |
|---|---|---|---|---|---|---|
| 0.12 | 0,018 | 0,004 | 0.05 | 0.02 | 0.05 | 0,001 |
| Mn | Si | FROM | Cr | Ti | Mo | Ni |
|---|---|---|---|---|---|---|
| 7.24 | 0.68 | 0.07 | 20.75 | 0.71 | 0.05 | 8.65 |
Position for welding:
H1, 2, P1, 2, H45, B1, T
Welding characteristics:
Good quality form filling, and root weld cladding layers, stable arcing. Weld metal welding wire used as well as argon (inert gas) environment.
Mechanical properties of weld metal (the test in the submerged arc welding)
| Brand welding wire | Elongation in% | Yield in σ T, MPa | Tensile strength σ B, in MPa | Toughness in KCU J / cm2 |
|---|---|---|---|---|
| CB-08H20N9G7T | 33 | 320.1 | 598.3 | 119.7 — 120.2 |
The weld metal is not prone to intergranular corrosion.
Buy at the best price
In stock company «Elektrovek-steel» offers a wide range of welding wire. Our offices are located in Russia and Ukraine. Making a purchase is possible, without leaving the office, through the Company’s website. All products have the highest quality. Technological equipment for each production stage gives us an opportunity to carry out individual orders in the event that the basic performance of the product does not satisfy you. We make quality custom orders of non-standard options, the timing of their implementation are minimal. When wholesale purchases discounts.