Designation
| Name |
The value |
| Designation GOST Cyrillic |
25ХГМ |
| Designation GOST Latin |
25XGM |
| Transliteration |
25HGM |
| By chemical elements |
25CrMnMo |
Description
25KHGM steel is used: for the manufacture of gear wheels gear boxes.
Note
Structural steel quality chromatorgraphy.
Standards
| Name |
Code |
Standards |
| Bars and shapes |
В32 |
GOST 4543-71, GOST 14955-77, TU 14-1-5414-2001, TU 14-1-2118-77, TU 14-1-3463-82, TU 14-11-245-88, TU 14-1-5228-93, TU 14-136-367-2008 |
| Bars and shapes |
В22 |
GOST 8319.0-75 |
| Blanks. Of the workpiece. Slabs |
В31 |
OST 3-1686-90, TU 14-1-4944-90 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Cu |
V |
Ti |
Mo |
W |
| GOST 4543-71 |
0.23-0.29 |
≤0.035 |
≤0.035 |
0.9-1.2 |
0.9-1.2 |
0.17-0.37 |
≤0.3 |
Rest |
≤0.3 |
≤0.05 |
≤0.03 |
0.2-0.3 |
≤0.2 |
Fe is the basis.
According to GOST 4543-71 the content in high-quality steel is regulated: P≤0,025%; S≤0.025%; Сu≤0.30%; in high-grade steel: P≤0,025%; S≤0.015%; Сu≤0.25%.
Mechanical properties
| Section, mm |
sT|s0,2, MPa |
σU, MPa |
d5, % |
y, % |
| Rolled steel. Quenching in oil from 860 °C to + Vacation at 200 °C, air cooling (longitudinal samples) |
| ≤50 |
≥1100 |
≥1200 |
≥10 |
≥45 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |
| y |
The relative narrowing |
Technological properties
| Name |
The value |
| Склонность к отпускной хрупкости |
Tend not. |
| Flock-sensitive sensitivity |
not sensitive. |