| Name | The value |
|---|---|
| Name | The value |
| Designation GOST Cyrillic | 15Х17АГ14 |
| Designation GOST Latin | 15X17AG14 |
| Transliteration | 15H17AG14 |
| By chemical elements | 15Cr17NMn14 |
| Name | The value |
|---|---|
| Name | The value |
| Designation GOST Cyrillic | ЭП213 |
| Designation GOST Latin | EP213 |
| Transliteration | EhP213 |
| By chemical elements | - |
15Х17АГ14 steel is used: for the manufacture of products operating in environments of weak aggressiveness and is recommended for slightly aggressive environments as a substitute for steel 12KH18N9. Steel good resistance to atmospheric corrosion.
Steel Nickel-free corrosion-resistant austenitic class.
| Name | Code | Standards |
|---|---|---|
| Name | Code | Standards |
| Classification, nomenclature and General rules | В30 | GOST 5632-72 |
| Blanks. Of the workpiece. Slabs | В31 | OST 3-1686-90 |
| Thermal and thermochemical treatment of metals | В04 | STP 26.260.484-2004 |
| Bars and shapes | В32 | TU 14-11-245-88 |
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | N | Ti | Mo |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | N | Ti | Mo |
| GOST 5632-72 | ≤0.15 | ≤0.03 | ≤0.05 | 13.5-15.5 | 16-18 | ≤0.8 | ≤0.6 | Rest | ≤0.3 | 0.25-0.37 | ≤0.2 | ≤0.3 |
| Section, mm | σU, MPa | d5, % |
|---|---|---|
| Section, mm | σU, MPa | d5, % |
| Bars hot rolled and forged at STP 26.260.484-2004. Quenching in water or air with 1030-1070 °C | ||
| ≥700 | ≥40 | |
| Name | The value |
|---|---|
| Name | The value |
| Weldability | difficult weldability |
| Features of heat treatment | Steel products for equipment of chemical industry termoobrabotannyj according to mode: heating to 1050±20 °C, the holding time at the heating for hardening to products with a wall thickness up to 10 mm - 30 min, over 10 mm - 20 min + 1 min per 1 mm max thickness cooling products with wall thickness up to 10 mm in the air, over 10 mm in water. |