02Х18Н11 steel is used: for the manufacture of products operating in nitric acid environments at elevated temperatures; for pipe billet production; equipment for chemical industry (nitric acid preheaters, evaporators ammonium nitrate, refrigerators capacitors, etc.); heat exchangers, condensers-oxidizers, tail gas heaters; for all connections of equipment installed in radioactive environments and in contact with aggressive environment.

Note

Low carbon steel corrosion resistant austenitic class.
Analogue steel 03Х18Н11 (Conclusion niikhimmash).

Standards

Name	Code	Standards
Name	Code	Standards
Bars and shapes	В22	GOST 1133-71, GOST 2590-2006
Welding and cutting metals. Soldering, riveting	В05	OST 95 10441-2002
Thermal and thermochemical treatment of metals	В04	STP 26.260.484-2004
Sheets and strips	В33	TU 14-1-3071-80, TU 14-1-2450-78, TU 14-1-5142-92
Blanks. Of the workpiece. Slabs	В31	TU 14-1-3183-81, TU 14-1-3931-84, TU 14-1-2132-77
Steel pipes and fittings to them	В62	TU 14-3-1401-86, TU 14-158-135-2003, TU 14-3-1339-85, TU 14-158-137-2003

Chemical composition

Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Mo
Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Mo
TU 14-1-3183-81	≤0.025	≤0.02	≤0.025	≤2	17-19	≤0.25	10.5-12.5	Rest	-
TU 14-158-137-2003	≤0.025	≤0.02	≤0.025	≤2	17-19	≤0.25	10.5-12.5	Rest	≤0.3

Fe is the basis.
According to TU 14-158-137-2003, cerium and other rare-earth metals can be introduced by 0.2-0.3%, which are not determined by chemical analysis.

Mechanical properties

Section, mm	s_T\|s_0,2, MPa	σ_U, MPa	d₅, %	y, %
Section, mm	s_T\|s_0,2, MPa	σ_U, MPa	d₅, %	y, %
Procurement of g/K and forged, billet. Quenching in water from 1080-1120°C (heat treated in cross-section 25 mm)
	≥186	≥480	≥45	-
Bars hot rolled and forged at STP 26.260.484-2004. Quenching in water from 1050-1100 °C
	≥200	≥520	≥45	≥50
Seamless cold-worked tubes-hardened state of delivery on the other 14-3-1401-86
	≥186	≥460	≥45	-

Description mechanical marks

Name	Description
Name	Description
s_T\|s_0,2	Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σ_U	Limit short-term strength
d₅	Elongation after rupture
y	The relative narrowing

Physical characteristics

Temperature	r, kg/m³
Temperature	r, kg/m³
20	7900

A description of the physical symbols

Name	Description
Name	Description
Е	The normal elasticity modulus
r	Density
l	Coefficient of thermal conductivity
R	UD. the resistivity

Technological properties

Name	The value
Name	The value
Weldability	automatic arc welding with non-consumable electrode in a continuous mode, manual argon arc welding with non-consumable electrode (filler or without filler material). Allowed the use of automatic arc welding submerged arc and manual arc welding with coated electrodes.
Microstructure	On the other 14-1-3183-81 content of alpha-phase should not exceed 1.0%.
Features of heat treatment	Steel products intended for use in aggressive environments and can be tempered, annealed. To ensure high corrosion resistance and an optimal combination of strength and plasticity of steel products are subjected to hardening from 1050-1100 °C and cooled in water or air. The holding time at the heating for hardening to products with a wall thickness up to 10 mm - 30 min, over 10 mm - 20 min + 1 min per 1 mm maximum thickness. In order to remove residual stresses resulting from the plastic deformation and welding, and also prevent warpage and stress corrosion cracking products is subjected to annealing at 870-900 °C, exposure time of 2-3 h, cooling with the furnace to 300 °C (speed of 50-100 °C/h), then - on the air.
Corrosion resistance	The steel is resistant to nitrous gases at temperatures up to +80 °C. Steel 02Х18Н11 has a high resistance to intergranular corrosion than steel of the brand 08KH18N10T and a high resistance to stab corrosion than steel of the brand 12Х18Н12Б.

Steel 02Х18Н11

Designation

Description