Designation
| Name |
The value |
| Designation GOST Cyrillic |
АМг3,5 |
| Designation GOST Latin |
AMg3,5 |
| Transliteration |
AMg35 |
| By chemical elements |
- |
Description
Alloy Amg3,5 is used: for the manufacture of semi-finished rolled by hot or cold deformation; details of aviation.
Note
The alloy system Al-Mg.
ISO 209−1 brand alloy Amg3,5 is designated AlMg3,5 and 5154.
Standards
| Name |
Code |
Standards |
| Non-ferrous metals, including rare, and their alloys |
В51 |
GOST 4784-97 |
| Bars and shapes |
В52 |
OST 1 92093-83 |
Chemical composition
| Standard |
Mn |
Cr |
Si |
Fe |
Cu |
Al |
Ti |
Zn |
Mg |
Be |
| GOST 4784-97 |
≤0.1 |
0.15-0.35 |
≤0.25 |
≤0.4 |
≤0.1 |
Rest |
≤0.2 |
≤0.2 |
3.1-3.9 |
≤0.0008 |
Al is the base.
According to GOST 4784-97, the total mass fraction of manganese and chromium should be in the range of 0.10-0.50%, the mass fraction of each other impurity (not regulated) ≤ 0.05%, the total mass fraction of other impurities ≤ 0.15%.
Physical characteristics
| Temperature |
r, kg/m3 |
| 20 |
2660 |
A description of the physical symbols
| Name |
Description |
| r |
Density |
Technological properties
| Name |
The value |
| Weldability |
The alloy is well welded all types of welding - TIG, contact, spot, and seam welding. Weld joint efficiency is 0.9-0.95 % of the strength of the basic material. |
| Pressure treatment |
Well-deformed in hot and cold condition. |
| Corrosion resistance |
Alloy with excellent General corrosion resistance, not cloned to stress corrosion cracking and intergranular corrosion (especially in the annealed condition). For additional protection parts against corrosion is anodizing or applied coatings. The corrosion resistance of the alloy (and the weld) high, is almost the same as that of pure aluminum. |
| Machinability |
Machinability is satisfactory. |