in Dnipro

Mülheim an der Ruhr
Dnieper
Kiev

Alloy САВ6

Alloy 1420 (01420)

Alloy 1980 (B48-4)

Alloy ABT101 (1901)

Alloy ABT102 (1903)

Alloy AB (1340)

Alloy AD31 (1310)

Alloy AD31E (1310E)

Alloy AD33 (1330)

Alloy AD35 (1350)

Alloy AK10 (SvAK10)

Alloy AK4 (1140)

Alloy AK4-1 (1141)

Alloy AK4-2 (1143)

Alloy AK6 (1360)

Alloy AK8 (1380)

Alloy AMg0.5 (1505)

Alloy AMG1 (1510)

Alloy AMg2 (1520)

Alloy AMg3 (1530)

Alloy AMg4 (1540)

Alloy AMg5 (1550)

Alloy AMg5P (1557)

Alloy AMg6 (1560)

Alloy AMg61 (1561)

Alloy AMg61H (1561H)

Alloy AMg63 (СвАМг63)

Alloy AMZ (1400)

Alloy AMTS (1401)

Alloy AMSh1 (AMSh-1)

Alloy APBA-1 (1551)

Alloy B65 (1165)

Alloy B91 (1913)

Alloy B92 (1920)

Alloy B93 (B93pch; 1930)

Alloy B94 (1940)

Alloy B95 (1950)

Alloy B95P (1957)

Alloy B96C (1960)

Alloy B96C3 (1965-1)

Alloy VD17 (1170)

Alloy D1 (1110)

Alloy D12 (1521)

Alloy D16 (1160)

Alloy D16P (1167)

Alloy D18 (1180)

Alloy D19 (1190)

Alloy D19P (1197)

Alloy D1P (1117)

Alloy D20 (1200)

Alloy D21 (1210)

Alloy D23 (WAD23; 1230)

Alloy D24 (VAD1; 1191)

Alloy K48-2 (1941)

Alloy K48-2pch (1943)

Alloy MM (1403)

Designation

Name	The value
Designation GOST Cyrillic	САВ6
Designation GOST Latin	CAB6
Transliteration	SAV6
By chemical elements	PbAlВ6

Description

Alloy САВ6 used: for the production of pressed extra virgin, rolled and drawn, depending on the wall thickness of pipes; castings; extruded rods ø 8−150 mm, used to manufacture parts for the aviation industry.

Standards

Name	Code	Standards
Tubes of non-ferrous metals and alloys	В64	TU 1-5-038-77, TU 1-5-076-77, TU 1-5-128-77, TU 1-5-207-98
Bars	В55	TU 1-5-088-77
Non-ferrous metals, including rare, and their alloys	В51	TU 1-5-140-78

Mechanical properties

Section, mm	σ_U, MPa	d
The pressed bars as supplied on the other 1-5-088-77. Hot-pressed or annealed (In cross-section of the specified diameter rod)
8-150	≥176	≥15
Tubes in the delivery condition on the other 1-5-038-77. Quenching + Natural aging
	≥176	≥12
Tubes in the delivery condition on the other 1-5-128-77. Quenching + Natural aging
	≥186	≥12

Description mechanical marks

Name	Description
σ_U	Limit short-term strength
d	Elongation after rupture

Technological properties

Name	The value
Macrostructure and pollution	The macrostructure of bars on the other 1-5-088-77 should not have cracks, utain, tears and segregated clusters. On microtemplate cut from rods are not permitted non-metallic inclusions larger than 0.5 mm in more than two on the bars with diameter up to 50 mm and more than 3 on the bars with the diameter more than 50 mm. of Surface defects on bars (films, layers, bubbles), viewed in microtemplate, not deducing the size of the rod for negative tolerance, acceptance a symptom of are not. The rods allowed for coarse grain rim, the value of which is not limited to, if the mechanical properties of quenched and naturally aged samples cut from the zone of coarse grain rim, will satisfy the requirements of TU 1-5-088-77. At the request of the consumer, coarse bezel may be limited, thus the full value of the rim is determined by agreement of the parties. To control the macrostructure of bars from ø20 mm and higher are cut template from utyaganovo end in the amount of 5% of the party, but not less than three rods. Control of the macrostructure of bars with a diameter less than 20 mm is not possible.
Microstructure	The microstructure of hardened bars on the other 1-5-088-77 should not have signs of burnout. Control of the microstructure at high temperatures to produce two samples, cut from two bars from the party.