Designation
| Name |
The value |
| Designation GOST Cyrillic |
4Х13Н6ЛВФ |
| Designation GOST Latin |
4X13H6LBF |
| Transliteration |
4H13N6LVF |
| By chemical elements |
4Cr13Н6BeWV |
| Name |
The value |
| Designation GOST Cyrillic |
ЭП354 |
| Designation GOST Latin |
EP354 |
| Transliteration |
EhP354 |
| By chemical elements |
- |
Description
4Х13Н6ЛВФ steel is used: for the manufacture of parts friction devices and assemblies (axles, bearings, slide valve steam, etc.), operating at temperatures up to 400 °C.
Standards
| Name |
Code |
Standards |
| Bars and shapes |
В32 |
TU 14-1-506-73 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
V |
Ti |
W |
Be |
| TU 14-1-506-73 |
0.3-0.5 |
≤0.025 |
≤0.03 |
≤0.6 |
12-14 |
≤0.6 |
5.5-6.5 |
Rest |
0.5-1 |
≤0.3 |
0.5-1 |
0.5-0.85 |
Fe is the basis.
According to TU 14-1-506-73, the chemical composition is given for steel grade 4Х13Н6ЛВФ-ВИ (ЭП354-ВИ).
Mechanical properties
| Section, mm |
HRC |
| Bars on the other 14-1-506-73. Quenching in water from 1000 °C + Two to four fold aging at 460-470 °C With exposure for an hour |
|
≥58 |
Description mechanical marks
| Name |
Description |
| HRC |
Rockwell hardness (indenter diamond spheroconical) |
Physical characteristics
| Temperature |
r, kg/m3 |
l, W/(m · °C) |
a, 10-6 1/°C |
С, J/(kg · °C) |
| 100 |
7740 |
19 |
124 |
460 |
A description of the physical symbols
| Name |
Description |
| Е |
The normal elasticity modulus |
Technological properties
| Name |
The value |
| The temperature of forging |
The forging temperature of 850-1100 °C. |
| Particularities of production of goods |
Bars at 14-1-506-73 THAT are delivered in heat treated condition for the regime: Normalizing at 950 °C + High tempering at 680 °C for 26 hours, air cooling. The hardness of steel in heat-treated bars shall not exceed 30 units HRC. |