Designation
| Name |
The value |
| Designation GOST Cyrillic |
45Х28Н49В5С |
| Designation GOST Latin |
45X28H49B5C |
| Transliteration |
45H28N49V5S |
| By chemical elements |
45Cr28Н49W5С |
Description
45Х28Н49В5С steel is used: for the manufacture of pipes tsentrobezhnolityh for the manufacture of the coils of the tubular furnace installations production of ammonia, hydrogen, ethylene, carbon disulphide, etc., operating in the temperature range 760−1060 °C and a pressure of 3.92 MPa (40 kgf/cm2); tsentrobezhnolityh pipes used as components in equipment for metallurgical, engineering, glass, ceramic, mining and processing petrochemical industry and is intended for the manufacture of blanks and parts used in the composition of the products of aviation and the nuclear industry.
Standards
| Name |
Code |
Standards |
| Steel pipes and fittings to them |
В62 |
TU 1333-047-00220302-02, TU 1333-003-76886532-2014 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Cu |
As |
V |
Ti |
Mo |
Zn |
Sn |
Pb |
W |
| TU 1333-003-76886532-2014 |
0.41-0.47 |
≤0.03 |
≤0.03 |
0.5005-1.51 |
26.5-29.5 |
0.9995-1.49 |
47.5-50.5 |
Rest |
≤0.2 |
≤0.01 |
0.0005-0.2 |
0.0005-0.1 |
≤0.5 |
≤0.01 |
≤0.01 |
≤0.01 |
4.5-5.5 |
Fe is the basis.
Mechanical properties
| sT|s0,2, MPa |
σU, MPa |
d |
| Tsentrobezhnolityh pipe outer diameter 85-320 mm. Quenching in water or air from 1100-1150 °C |
| ≥295 |
≥490 |
≥5 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d |
Elongation after rupture |