Steel 015Х18Н15Р17 (ЭП167А)

Designation

Name The value
Designation GOST Cyrillic 015Х18Н15Р17
Designation GOST Latin 015X18H15P17
Transliteration 015H18N15R17
By chemical elements 015Cr18Н15B17
Name The value
Designation GOST Cyrillic ЭП167А
Designation GOST Latin EP167A
Transliteration EhP167A
By chemical elements -

Description

015Х18Н15Р17 steel is used: for the manufacture of pipes used in chemical engineering.

Note

Hromonikelevoj corrosion and heat resistant steel, alloyed by boron.

Standards

Name Code Standards
Blanks. Of the workpiece. Slabs В31 TU 14-1-2816-79

Chemical composition

Standard C S P Mn Cr Si Ni Fe B Nb
TU 14-1-2816-79 ≤0.015 ≤0.2 ≤0.2 0.6-1.1 17-19 ≤0.6 14-16 Rest ≤0.17 0.1-0.4
Fe is the basis.
According to TU 14-1-2816-79 the chemical composition is given for steel grade 015Х18Н15Р17-ВД (ЭП167А-ВД). In the finished metal, the aluminum content is not more than 0.30%, nitrogen is not more than 0.050%. In the finished metal, the content of cobalt is controlled, the results of the control are not a defective feature, but are indicated in the certificate. By agreement of the parties, the pipe billet is supplied with a cobalt content of not more than 0.0050%. In the finished metal, if the requirements of TU are complied with, the deviation by the content of carbon + 0.0050%, the boron content ± 0.040% is permissible.

Mechanical properties

Section, mm sT|s0,2, MPa σU, MPa d5, %
Tubular billet on the other 14-1-2816-79. Quenching in water from 950-970 °C
≥186 ≥470 ≥35
≥137 ≥340 ≥26

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σU Limit short-term strength
d5 Elongation after rupture