Designation
| Name |
The value |
| Designation GOST Cyrillic |
ХН60М |
| Designation GOST Latin |
XH60M |
| Transliteration |
HN60M |
| By chemical elements |
CrNi60Cu |
| Name |
The value |
| Designation GOST Cyrillic |
ЭП367 |
| Designation GOST Latin |
EP367 |
| Transliteration |
EhP367 |
| By chemical elements |
- |
| Name |
The value |
| Designation GOST Cyrillic |
06Х15Н60М1 |
| Designation GOST Latin |
06X15H60M1 |
| Transliteration |
06H15N60M1 |
| By chemical elements |
06Cr15Ni60Cu1 |
Description
Alloy ХН60М used: for the manufacture of forged bars with diameter of 60−100 mm; details of aircraft and special equipment, welding wire and electrodes.
Note
High-temperature Nickel-based alloy.
The recommended maximum operating temperature for a limited time 750 °C.
The temperature of beginning of intensive scaling in air 1000 °C.
Standards
| Name |
Code |
Standards |
| Welding and cutting metals. Soldering, riveting |
В05 |
TU 14-1-2370-78 |
| Bars and shapes |
В32 |
TU 14-1-2693-79 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Mo |
| TU 14-1-2693-79 |
≤0.08 |
≤0.015 |
≤0.015 |
1-2 |
14-16 |
≤0.5 |
Rest |
≤4 |
14-16 |
Ni is the basis.
According to TU 14-1-2370-78, the chemical composition is given for the welding wire of the brand Sv-06Kh15N60M15 (EP367).
According to TU 14-1-2693-79, the chemical composition is given for forged bars of the alloy KhN60M (06H15N60M15, EPZ67). In the finished metal, deviations in chemical composition are allowed: for silicon + 0.020%, for manganese ± 0.050%, for chromium ± 0.20%, for molybdenum ± 0.10%.
Mechanical properties
| Section, mm |
sT|s0,2, MPa |
σU, MPa |
d5, % |
| The welding wire supplied on the other 14-1-2370-78 |
| ≤2 |
- |
≤1667 |
- |
| Bars hot rolled and forged on the other 14-1-2693-79. Quenching in water from 1140-1160 °C. Samples of the longitudinal |
|
≥295 |
≥780 |
≥45 |
| The welding wire supplied on the other 14-1-2370-78 |
| 2 |
- |
≤1080 |
- |
| Bars hot rolled and forged on the other 14-1-2693-79. Quenching in water from 1140-1160 °C. Samples of the longitudinal |
|
≥196 |
≥540 |
≥30 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |
Technological properties
| Name |
The value |
| Macrostructure and pollution |
Macrostructure of steel bars on the other 14-1-2693-79 should not have shrinkage and looseness, bubbles, cracks, inclusions and delaminations are visible without using the magnifying devices. Rejection feature is the presence of a signal from the defect, the amplitude of which is greater than or equal to the amplitude of the signal reflected from the reference reflector with a diameter of 3.0 mm reference sample sensitivity set on the same with a tolerance of minus 10% or a greater depth. |