| Designation GOST Cyrillic | 110Г13ХБРЛ |
| Designation GOST Latin | 110G13XBPL |
| Transliteration | 110G13HBRL |
| By chemical elements | 110Mn13CrNbB |
110G13KHBRL steel is used: for the manufacture of castings of the teeth of excavator buckets, crawler links, working bodies crushing equipment.
Steel wear-resistant austenitic class. The steel has a high resistance to wear when exposed to high pressures or shock loads.
| Name | Code | Standards |
|---|---|---|
| Name | Code | Standards |
| Castings with special properties (iron and steel) | В83 | GOST 21357-87 |
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | B | Nb |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | B | Nb |
| GOST 21357-87 | 0.9-1.3 | ≤0.02 | ≤0.02 | 11.5-14.5 | 0.8-1.5 | 0.3-0.9 | ≤0.3 | Rest | ≤0.3 | 0.002-0.005 | 0.06-0.1 |
| sT|s0,2, MPa | σU, MPa | d | y, % | HB, MPa |
|---|---|---|---|---|
| sT|s0,2, MPa | σU, MPa | d | y, % | HB, MPa |
| Casting. Quenching in water from 1050-1100 °C (after heat treatment d. b. purely austenitic structure) | ||||
| ≥480 | ≥750 | ≥20 | ≥30 | ≥190 |