Designation
| Name |
The value |
| Designation GOST Cyrillic |
09Х16Н7М2Ю |
| Designation GOST Latin |
09X16H7M2Ju |
| Transliteration |
09H16N7M2Yu |
| By chemical elements |
09Cr16Н7Mo2Al |
| Name |
The value |
| Designation GOST Cyrillic |
ЗИ65 |
| Designation GOST Latin |
ZI65 |
| Transliteration |
ZI65 |
| By chemical elements |
ЗИ65 |
Description
09Х16Н7М2Ю steel is used: for the production of hot rolled and forged long products metal used for manufacture of units and parts of power engineering by cold machining.
Standards
| Name |
Code |
Standards |
| Bars and shapes |
В32 |
TU 14-1-1396-75 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Cu |
Al |
Mo |
| TU 14-1-1396-75 |
≤0.09 |
≤0.03 |
≤0.03 |
≤0.7 |
15-16.5 |
≤0.7 |
6.5-7.5 |
Rest |
≤0.3 |
0.5-1 |
1-2 |
Fe is the basis.
According to TU 14-1-1396-75 deviations from the norms of chemical composition are allowed: by the content of chromium ± 0.30%, by the nickel content ± 0.20%. The content of residual elements must comply with GOST 5632. Upon agreement with the customer, the specification of the chemical composition of steel specified in this Specification may be specified.
Mechanical properties
| Section, mm |
sT|s0,2, MPa |
σU, MPa |
d5, % |
y, % |
KCU, kJ/m2 |
| Hot rolled and forged long products metal on the other 14-1-1396-75. Quenched from 940-960 °C cold treatment at -70±10 °C for 2 hours + Vacation at 390-410 °C (extract 3 hours), air cooling |
|
≥900 |
≥1100 |
≥10 |
≥40 |
≥392 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |
| y |
The relative narrowing |
| KCU |
Toughness |
Technological properties
| Name |
The value |
| Macrostructure and pollution |
The macrostructure of the steel on the other 14-1-1396-75 on cross etched templeto should not be visible without using the magnifying devices of the traces of shrinkage, bubbles, cracks, and slag inclusions. The permissible defects of the macrostructure scores in the scales GOST 10243 shall not exceed at the point of heterogeneity, Central porosity and phase separation the square of the 2nd score; intergranular cracks - 3 points. |