08Х14МФ steel is used: for the production of billets and bars intended for the manufacture of pipes; steam boilers, steam pipelines and collectors with high and supercritical steam parameters; parts and equipment, power engineering, nuclear and thermal power plants.

Note

High-chromium steel martensite-ferritic class.

Standards

Name	Code	Standards
Bars and shapes	В32	TU 14-1-1529-2003
Sheets and strips	В33	TU 14-105-549-92
Steel pipes and fittings to them	В62	TU 14-3-1808-91, TU 1361-023-00212179-2005

Chemical composition

Standard	C	S	P	Mn	Cr	Si	Fe	V	Mo
TU 14-1-1529-2003	0.05-0.1	≤0.02	≤0.035	0.8-1.2	13-14.8	0.2-0.45	Rest	0.15-0.3	0.2-0.4

Fe is the basis.
According to TU 14-1-1529-2003, the mass fraction of the residual elements: tungsten, nickel and copper should meet the requirements of GOST 5632. For steel 08Х14МФ-Ш the sulfur content should be ≤ 0,15% phosphorus content ≤ 0,35%.

Mechanical properties

Section, mm	s_T\|s_0,2, MPa	σ_U, MPa	d₅, %
The tubular billet. Normalization at 1000-1030 °C, air cooling + Vacation at 750-770 °C (aged for at least 3 h), air cooling
25	≥345	≥540	≥20
Pipe seamless cold and warm on the other 1361-023-00212179-2005
-	245-392	≥441	≥25
-	≥196	-	-
-	≥176	-	-
-	245-490	≥441	≥25

Description mechanical marks

Name	Description
s_T\|s_0,2	Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σ_U	Limit short-term strength
d₅	Elongation after rupture

Technological properties

Name	The value
Weldability	Has good weldability.
Corrosion resistance	Stainless steel, corrosion resistant, okolnostima steel.