Steel 43Х3СНМВФА (СП43)
Designation
Description
43Х3СНМВФА steel is used: for the manufacture of various items of heavy and power engineering.
Standards
Chemical composition
Fe is the basis.
According to TU 14-1-871-74 the chemical composition is given for steel SP43-VD.
According to TU 14-1-4461-88, the chemical composition of the steel should comply with the standards specified in Table 2 (Appendix 1), sent on request by the Central Research Institute of Chemical Technology named after Bardin. The sulfur content of sulfur is not more than 0.011%, phosphorus is not more than 0.015%, while the total content of sulfur and phosphorus should not be more than 0.022%. The residual copper content should not be more than 0.15%. With the consent of the consumer, it is allowed - up to 0.20%. In the finished sheets the following deviations in chemical composition from the norms indicated in Table 2 are allowed: carbon + 0.02 / -0.010%; tungsten ± 0.10%; manganese, silicon, chromium and nickel ± 0.050%; molybdenum ± 0.030%; vanadium +0.020%. Partial or complete replacement of tungsten by molybdenum from the calculation of 2.5 mass fraction of tungsten is allowed with one mass fraction of molybdenum.
According to TU 14-1-871-74 the chemical composition is given for steel SP43-VD.
According to TU 14-1-4461-88, the chemical composition of the steel should comply with the standards specified in Table 2 (Appendix 1), sent on request by the Central Research Institute of Chemical Technology named after Bardin. The sulfur content of sulfur is not more than 0.011%, phosphorus is not more than 0.015%, while the total content of sulfur and phosphorus should not be more than 0.022%. The residual copper content should not be more than 0.15%. With the consent of the consumer, it is allowed - up to 0.20%. In the finished sheets the following deviations in chemical composition from the norms indicated in Table 2 are allowed: carbon + 0.02 / -0.010%; tungsten ± 0.10%; manganese, silicon, chromium and nickel ± 0.050%; molybdenum ± 0.030%; vanadium +0.020%. Partial or complete replacement of tungsten by molybdenum from the calculation of 2.5 mass fraction of tungsten is allowed with one mass fraction of molybdenum.