Designation
| Name |
The value |
| Designation GOST Cyrillic |
АМг4К1,5М |
| Designation GOST Latin |
AMg4K1,5M |
| Transliteration |
AMg4K15M |
| By chemical elements |
- |
| Name |
The value |
| Designation GOST Cyrillic |
АМг4К1,5М1 |
| Designation GOST Latin |
AMg4K1,5M1 |
| Transliteration |
AMg4K15M1 |
| By chemical elements |
- |
Description
Alloy Amg4k1,5M is used: for the manufacture of ingots and shaped casting in a metal mold.
Note
Aluminum foundry alloy system Al-Mg.
Standards
| Name |
Code |
Standards |
| Non-ferrous metals, including rare, and their alloys |
В51 |
GOST 1583-93 |
| Castings, non-ferrous metals and alloys |
В84 |
OST 1 80029-83 |
Chemical composition
| Standard |
Mn |
Si |
Fe |
Cu |
Al |
Ti |
Zn |
Mg |
Be |
| GOST 1583-93 |
0.6-0.9 |
1.3-1.7 |
≤0.4 |
0.7-1 |
Rest |
0.1-0.25 |
≤0.1 |
4.5-5.2 |
0.002-0.004 |
Al is the base.
According to GOST 1583-93, the iron content is indicated for pressure. The amount of allowable impurities should be for die casting ≤ 0.30%.
Mechanical properties
| σU, MPa |
d |
HB, MPa |
| Casting. T6 mode: two-stage heating: 540-550 °C (aging 5-9 h) + 540-548 °C (aging 5-9 hours), quenching in water with a temperature of 80-100 °C to + Complete artificial aging at 165-175 °C (delay of 6-10 h) |
| ≥265 |
≥2.3 |
≥104 |
Description mechanical marks
| Name |
Description |
| σU |
Limit short-term strength |
| d |
Elongation after rupture |
| HB |
Brinell hardness number |