Designation
| Name |
The value |
| Designation GOST Cyrillic |
АК9Ц6 |
| Designation GOST Latin |
AK9Ts6 |
| Transliteration |
AK9Ts6 |
| By chemical elements |
- |
| Name |
The value |
| Designation GOST Cyrillic |
АК9Ц6р |
| Designation GOST Latin |
AK9Ts6p |
| Transliteration |
AK9Ts6r |
| By chemical elements |
- |
Description
Alloy AK9C6 used: for the manufacture of ingots and shaped castings.
Note
Aluminum foundry alloy of the system Al-Si-Zn.
Standards
| Name |
Code |
Standards |
| Non-ferrous metals, including rare, and their alloys |
В51 |
GOST 1583-93 |
| Castings, non-ferrous metals and alloys |
В84 |
OST 1 80029-83 |
Chemical composition
| Standard |
Mn |
Si |
Ni |
Fe |
Cu |
Al |
Zn |
Mg |
| GOST 1583-93 |
0.1-0.6 |
8-10 |
≤0.3 |
0.3-1 |
0.3-1.5 |
Rest |
5-7 |
0.3-0.5 |
Al is the base.
The amount of allowable impurities should be for die casting casting ≤ 0.60%. The total content of lead and tin should be ≤ 0.30.
Mechanical properties
| σU, MPa |
d |
HB, MPa |
| Casting. Without heat treatment |
| ≥147 |
≥0.8 |
≥70 |
| ≥167 |
≥0.8 |
≥80 |
Description mechanical marks
| Name |
Description |
| σU |
Limit short-term strength |
| d |
Elongation after rupture |
| HB |
Brinell hardness number |