Steel SV-10НЮ

  • Steel Sv-10GN3SMD
  • Sv-08GSMT steel
  • Steel Sv-08H15N23V7G7M2 (EP88)
  • Steel Св-08Х19Н10Г2Б (ЭИ898; Н-89)
  • Steel Sv-08X1Du
  • Steel Св-08Х20Н9С2БТЮ (EP156)
  • Steel Св-08Х25Н20С3Р1 (EP532)
  • Steel Sv-08HG2SDU
  • Sv-08HN2GMTA steel
  • Sv-09HNMTA steel
  • Sv-09HNMTAA steel
  • Sv-09HN4MDTA steel
  • Sv-10HN1MA steel
  • Sv-10HN2SMD steel
  • Sv-08GM steel
  • Sv-10GSM steel
  • Sv-10Nu steel
  • Steel Sv-10Kh16N25AM6 (EI395; H-66)
  • Steel Св-10Х16Н25М6АФ (ЗИ112)
  • Steel Sv-10H19N11M4F (EP647)
  • Sv-10H19H23G2M5FAT (EP868)
  • Steel Sv-10Х21Н11ФТ (EP854)
  • Sv-10X2M steel
  • Sv-10HGSN2MT steel
  • Sv-10KhMFTU steel
  • Sv-10KhMFTU-A steel
  • Sv-12M steel
  • Sv-12Kh2NMA steel
  • Steel Sv-06H15N35G7M6B (EP582)
  • Steel Sv-01Kh12N6M (ChS48)
  • Steel Св-01Х19Н18Г10АМ4 (EP690)
  • Steel Sv-03GKhN2MD
  • Steel Sv-03GKhN3MD
  • Steel Sv-03HN3MD
  • Sv-04N2GSTA steel
  • Sv-04N2GTA steel
  • Sv-04N3GMTA steel
  • Sv-04N3GSMTA steel
  • Steel Sv-04H19H11M3 (H-65)
  • Sv-04Cr19Ni (04Cr19N9) steel
  • Sv-04H20N10G2B (EP762)
  • Sv-06H14GMFBA steel
  • Steel Sv-08GN2SMD
  • Steel Sv-06Х21Н7БТ (EP500)
  • Sv-06Cr3G2SmFtu4 steel
  • Sv-06Kh8G2SMFtu4 steel
  • Steel Sv-07H22H13G5ST (ChS49)
  • Steel Sv-07Cr25H13 (H-71)
  • Steel Sv-07CGSN3MD
  • Steel Sv-07HN3MD
  • Sv-08 steel
  • Sv-08G1NMT steel
  • Sv-08G1S steel
  • Sv-08G2SM steel
  • Sv-08G2SNMT steel
  • Sv-08G2SNTYR steel

    • Designation

    Name The value
    Designation GOST Cyrillic Св-10НЮ
    Designation GOST Latin Cb-10HJu
    Transliteration Sv-10NYu
    By chemical elements 10НAl

    Description

    Steel SV-10НЮ used: for the production of welding wires for electroslag and automatic submerged arc welding steel of the type 12KHM.

    Note

    A steel alloy.

    Standards

    Name Code Standards
    Bars and shapes В32 TU 14-1-2203-77
    Welding and cutting metals. Soldering, riveting В05 TU 14-1-2219-77

    Chemical composition

    Standard C S P Mn Cr Si Ni Fe Cu Al Ti Ce
    TU 14-1-2219-77 ≤0.1 ≤0.03 ≤0.03 0.4-0.7 ≤0.25 ≤0.03 1.5-1.9 Rest ≤0.25 0.1-0.25 ≤0.1 -
    TU 14-1-2203-77 ≤0.1 ≤0.03 ≤0.03 0.4-0.7 ≤0.25 ≤0.03 1.5-1.9 Rest ≤0.25 0.1-0.25 ≤0.1 0.1
    Fe is the basis.
    According to TU 14-1-2219-77 the chemical composition is given for steel grade Sv-10NYu. Permissible deviations from the chemical composition: carbon ± 0.010%, manganese ± 0.040%, silicon ± 0.070%, nickel ± 0.050%, aluminum ± 0.020%. Cerium is introduced in the form of ferrocerium at a rate of 1 kg per 1 ton of liquid metal and its residual content is not determined.
    According to TU 14-1-2203-77, the chemical composition is given for the S-10NYu welding wire. In rod, not intended for copper-clad wire, the copper content should not exceed 0.25%, and at the request of the consumer - not more than 0.20%. Cerium is introduced by calculation at 0.10%.

    Mechanical properties

    Section, mm σU, MPa
    The welding wire of the highest quality cold-worked state beyond 14-1-2219-77
    3 736-981
    4 589-834
    5 539-785

    Description mechanical marks

    Name Description
    σU Limit short-term strength

    Technological properties

    Name The value
    Macrostructure and pollution In the macrostructure of wire rod, are not allowed discontinuity of the metal caused by the presence of shrinkage, axial looseness, bubbles, cracks, delamination and inclusions.
    Microstructure Wire rod microstructure should be uniform. Padalka (martensitic and toostonedtocare areas) is not allowed.
    Particularities of production of goods The welding wire first quality class on the other 14-1-2219-77 supplied in cold-worked condition, without determining the mechanical properties.