Steel SV-04Х20Н10Г2Б used: for the production of welding of the ribbon thickness of 0.5 and 0.7 mm and the wire from 1.2 mm to 5.0 mm, used for hardfacing of parts and for welding of steel structures in nuclear power engineering.

Note

Corrosion-resistant steel.

Standards

Name	Code	Standards
Welding and cutting metals. Soldering, riveting	В05	TU 14-1-2270-77, TU 14-1-4591-89, TU 14-1-5363-2008
Tape	В34	TU 14-1-2270-2013

Chemical composition

Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Nb
TU 14-1-2270-2013	≤0.04	≤0.018	≤0.025	1.8-2.2	18.5-20.5	0.2-0.45	9-10.5	Rest	0.9-1.3

Fe is the basis.
According to TU 14-1-2270-2013, deviations in the mass fraction of carbon are allowed: plus 0.0050%. Permissible deviations in the mass fraction of the remaining elements in accordance with Table 3 of GOST 2246. Upon agreement of the consumer with the supplier, it is allowed to limit the mass fraction of carbon, sulfur, phosphorus and rationing the residual mass fraction of elements in steel: cobalt, aluminum, copper and nitrogen.

Mechanical properties

Section, mm	σ_U, MPa
Tape welding on delivery on the other 14-1-2270-2013
	880-1127
Tape welding on the other 14-1-2270-77
	≤1130

Description mechanical marks

Name	Description
σ_U	Limit short-term strength

Technological properties

Name	The value
Microstructure	The amount of ferritic phase in steel should be in the range of 4.0 to 8.0%.

Steel SV-04Х20Н10Г2Б (ЭП762)

Designation

Description