Molybdenum MK

Designation

Name	The value
Designation GOST Cyrillic	МК
Designation GOST Latin	MK
Transliteration	MK
By chemical elements	Cu

Description

Molybdenum MK is used: for the manufacture of wire with a diameter of from 200 to 1000 µm, obtained by powder metallurgy and used for the manufacture of parts for various applications in electronic products.

Note

Molybdenum with a silica-doped, characterized by much higher temperature rekristallizatsiya higher tensile strength and bending in the annealed condition, the molybdenum than other brands.

Standards

Name	Code	Standards
Wire from nonferrous metals and their alloys	В74	OST 11 021.004-76

Chemical composition

Standard	Si	Mo
OST 11 021.004-76	0.02-0.04	≥99.92

Mo is the basis.
According to the OST 11 021.004-76 chemical composition is given for molybdenum grade MK. The total mass fraction of impurities should not be more than 0.040%. The amount of impurities includes the following elements: calcium, magnesium, nickel, iron, aluminum, if they are not additives.

Mechanical properties

Section, mm	σ_U, MPa	d
Wire as supplied at OST 11 021.004-76. In the column cross-section specified the wire diameter in µm
200-400	≥1197	≥2
400-1000	≥981	≥3
200-400	≥804	≥2
400-1000	≥687	≥3

Description mechanical marks

Name	Description
σ_U	Limit short-term strength
d	Elongation after rupture

Technological properties

Name	The value
Particularities of production of goods	For OST 11 021.004-76 wire micron size range comes in the following six groups: A. Wire having on a surface layer of the technological lubricant; B. Wire, free from technological lubricant by electrochemical etching method; B. Wire, annealed to the required mechanical properties, Wire, purified by the method of electrochemical etching and annealed to the required mechanical properties; D. Wire, annealed to the required mechanical properties. Compared to the wire group has higher strength and less elongation; E. Wire, purified by the method of electrochemical etching and annealed to the required mechanical properties. Compared with the wire of the group G has a higher coefficient "K" and a smaller elongation.