Brass LS58-3

  • Brass LO70-1
  • Brass LMZA57-3-1
  • Brass LMzAJKS70-7-5-2-2-1
  • Brass LMZh57-1,5-0,75
  • Brass LMtsKA58-2-1-1
  • Brass LMtsKNS58-3-1,5-1,5-1
  • Brass LMtsKNSA58-3-1,5-1,5-1
  • Brass LMtsSKa58-2-2-1-1
  • Brass LMsh68-0,05
  • Brass LN65-5
  • Brass LNKMts49-10-0,3-0,2
  • Brass LNKoMts49-9-0,2-0,2
  • Brass ЛНМц60-9-5
  • Brass LO60-1
  • Brass LO62-1
  • Brass LKS65-1,5-3
  • Brass LO90-1
  • Brass LOK59-1-0.3
  • Brass LOMNA49-0,5-10-0,4-0,4
  • Brass Lomsh70-1-0.04
  • Brass Lomsh70-1-0.05
  • Brass LS58-2
  • Brass LS58-3
  • Brass LS59-1
  • Brass LS59-1B
  • Brass LS59-2
  • Brass LS60-1
  • Brass LS63-3
  • Brass LS64-2
  • Brass LS74-3
  • Brass LA85-0.5
  • Brass L59
  • Brass L60
  • Brass L63
  • Brass L66
  • Brass L68
  • Brass L70
  • Brass L72
  • Brass L75mk
  • Brass L80
  • Brass L85
  • Brass L90
  • Brass L96
  • Brass LA77-2
  • Brass LA77-2u
  • Brass LMZ58-2
  • Brass LAJ60-1-1 (LAJ60-1-1L)
  • Brass LAZHMTS52-2-1-1,5-1
  • Brass LAMsh77-2-0,04
  • Brass LAMSh77-2-0,05
  • Brass LAN59-3-2
  • Brass LANKMZ 75-2-2,5-0,5-0,5 (alloy 156)
  • Brass LAF94-0,5-0,15
  • Brass LZMc59-1-1
  • Brass LZhS58-1-1
  • Brass LC62-0.5
  • Brass LK75B
  • Brass LCAN80-1-1,9-5,8
  • Brass ЛКАНМЦ75-2-2,5-0,5-0,5
  • Brass LCBO62-0,2-0,04-0,5

    • Designation

    Name The value
    Designation GOST Cyrillic ЛС58-3
    Designation GOST Latin LC58-3
    Transliteration LS58-3
    By chemical elements ЛPb58-3

    Description

    Brass LS58−3 is used: for the manufacture of semi-finished products (rods, tubes, strips); parts for various industrial uses by machining.

    Note

    Lead brass.

    Standards

    Name Code Standards
    Tape В54 GOST 15527-2004
    Bars В55 GOST 2060-2006, GOST Р 52597-2006, GOST 31366-2008
    Non-ferrous metals, including rare, and their alloys В51 GOST 28873-90
    Sheets and strips В53 TU 48-21-364-79
    Tubes of non-ferrous metals and alloys В64 TU 48-21-880-89

    Chemical composition

    Standard Ni Fe Cu Al Zn Sn Pb
    GOST 15527-2004 ≤0.5 ≤0.5 57-59 ≤0.1 Rest ≤0.4 2.5-3.5
    Cu is the basis.
    According to GOST 15527-2004, GOST 2060-2006, the sum of other elements should be ≤ 0,20%. In brass, the mass fraction of nickel is allowed up to 1.0% due to the mass fraction of copper, which is not taken into account in the sum of other impurities.

    Mechanical properties

    Section, mm σU, MPa d5, % d10 HB, MPa HV, MPa
    Rods are supplied according to GOST 2060-2006 (longitudinal samples)
    10-50 ≥360 ≥22 ≥18 - 80-140
    55-180 ≥360 ≥22 ≥18 - 70-140
    3-50 ≥330 ≥25 ≥22 ≥80 80-140
    13-20 ≥390 ≥15 ≥12 ≥100 121-170
    21-40 ≥390 ≥18 ≥15 ≥100 121-170
    3-12 ≥410 ≥10 ≥8 ≥100 121-170
    3-12 ≥490 ≥7 ≥5 ≥130 ≥171

    Description mechanical marks

    Name Description
    σU Limit short-term strength
    d5 Elongation after rupture
    d10 Elongation after rupture
    HB Brinell hardness number
    HV The Vickers hardness

    Physical characteristics

    Temperature r, kg/m3
    20 8450

    A description of the physical symbols

    Name Description
    Е The normal elasticity modulus
    l Coefficient of thermal conductivity
    R UD. the resistivity