Bronze Bro3c12s5 (БрОЦС3-12-5)

  • Bronze БрО3Ц8С4Н1 (БрОЦСН3-8-4-1)
  • Bronze БрО8Ц4 (БрОЦ8-4)
  • Bronze БрО8С21 (БрОС8-21)
  • Bronze БрО8С12 (БрОС8-12)
  • Bronze БрО8Н4Ц2 (БрОНЦ8,5-4-2)
  • Bronze БрО6Ц6С3 (БрОЦС6-6-3)
  • Bronze БрО6Ц6С2х (БрОЦС6-6-2х)
  • Bronze БрО6Ц4С2Н1 (БрОЦСН6-4-2-1)
  • Bronze БрО6С6Ц3
  • Bronze БрО6К2Ц1
  • Bronze БрО5Ц6С5 (БрОЦС5-6-5)
  • Bronze БрО5Ц5С5 (БрОЦС5-5-5)
  • Bronze БрО5С25 (БрОС5-25)
  • Bronze БрО4Ц8С5
  • Bronze БрО4Ц7С5 (БрОЦС3,5-7-5)
  • Bronze БрО4Ц4С17 (БрОЦС4-4-17)
  • Bronze БрО3Ц7С5Н1 (БрОЦСН3-7-5-1)
  • Bronze БрО3Ц6С5 (БрОЦС3-6-5)
  • Bronze БрО3Ц13С4 (БрОЦС3-13-4)
  • Bronze БрО3Ц12С5 (БрОЦС3-12-5)
  • Bronze БрО3,5Ц7С5
  • Bronze BrO19
  • Bronze БрО16С5 (БрОС16-5)
  • Bronze БрО10Ц2Н2 (БрОЦН10-2-2)
  • Bronze БрО10Ц2Н1,5 (БрОЦН10-2-1,5)
  • Bronze БрО10Ц2 (БрОЦ10-2)
  • Bronze БрО10Ф1 (БрОФ10-1)
  • Bronze БрО10Ф0,7Н0,5 (БрОФН10-0,7-0,5)
  • Bronze БрО10С2Н3 (БрОСН10-2-3)
  • Bronze БрО10С10 (БрОС10-10)

    • Designation

    Name The value
    Designation GOST Cyrillic БрО3Ц12С5
    Designation GOST Latin BpO3Ts12C5
    Transliteration BrO3Ts12S5
    By chemical elements BaSn3Zn12Pb5
    Name The value
    Designation GOST Cyrillic БрОЦС3-12-5
    Designation GOST Latin BpOTsC3-12-5
    Transliteration BrOTsS3-12-5
    By chemical elements BaSnZnPb3-12-5

    Description

    Bronze Bro3c12s5 used: for the production of castings of valves General purpose; details of pipeline valves and actuators to it.

    Standards

    Name Code Standards
    Bars В55 GOST 24301-93
    Non-ferrous metals, including rare, and their alloys В51 GOST 613-79
    Cast iron castings (grey and malleable cast iron) В81 OST 24.207.01-90

    Chemical composition

    Standard S P Si Ni Fe Cu As Al Zn Sn Sb Pb Mg
    GOST 613-79 ≤0.05 ≤0.05 ≤0.02 ≤2 ≤0.4 Rest ≤0.15 ≤0.02 8-15 2-3.5 ≤0.5 3-6 ≤0.02
    Cu is the basis.
    According to GOST 613-79, the total content of impurities should be ≤ 1.30%. Impurities not regulated by the standard are included in the total amount of impurities. The sum of impurities of silicon and aluminum should not exceed 0.020%. In bronze, not intended for casting parts operating under hydraulic pressure, the manufacturer's agreement with the consumer allows the mass fraction of aluminum to 0.050% and silicon - up to 0.050%. The mass fraction of nickel due to copper and the sum of impurities is not included.

    Mechanical properties

    Section, mm σU, MPa d5, % HB, MPa
    Castings are supplied without heat treatment
    - ≥206 ≥5 ≥60
    - ≥176 ≥8 ≥60
    Rods and tubes of the first group is made by a horizontal molding according to GOST 24301-93 (in parentheses are the values for the casting of the second group of castings)
    ≥220 (180) ≥20 (16) ≥65 (60)

    Description mechanical marks

    Name Description
    σU Limit short-term strength
    d5 Elongation after rupture
    HB Brinell hardness number