Bronze БрО10Ц2Н1,5 (БрОЦН10-2-1,5)

  • Bronze БрО3Ц8С4Н1 (БрОЦСН3-8-4-1)
  • Bronze БрО8Ц4 (БрОЦ8-4)
  • Bronze БрО8С21 (БрОС8-21)
  • Bronze БрО8С12 (БрОС8-12)
  • Bronze БрО8Н4Ц2 (БрОНЦ8,5-4-2)
  • Bronze БрО6Ц6С3 (БрОЦС6-6-3)
  • Bronze БрО6Ц6С2х (БрОЦС6-6-2х)
  • Bronze БрО6Ц4С2Н1 (БрОЦСН6-4-2-1)
  • Bronze БрО6С6Ц3
  • Bronze БрО6К2Ц1
  • Bronze БрО5Ц6С5 (БрОЦС5-6-5)
  • Bronze БрО5Ц5С5 (БрОЦС5-5-5)
  • Bronze БрО5С25 (БрОС5-25)
  • Bronze БрО4Ц8С5
  • Bronze БрО4Ц7С5 (БрОЦС3,5-7-5)
  • Bronze БрО4Ц4С17 (БрОЦС4-4-17)
  • Bronze БрО3Ц7С5Н1 (БрОЦСН3-7-5-1)
  • Bronze БрО3Ц6С5 (БрОЦС3-6-5)
  • Bronze БрО3Ц13С4 (БрОЦС3-13-4)
  • Bronze БрО3Ц12С5 (БрОЦС3-12-5)
  • Bronze БрО3,5Ц7С5
  • Bronze BrO19
  • Bronze БрО16С5 (БрОС16-5)
  • Bronze БрО10Ц2Н2 (БрОЦН10-2-2)
  • Bronze БрО10Ц2Н1,5 (БрОЦН10-2-1,5)
  • Bronze БрО10Ц2 (БрОЦ10-2)
  • Bronze БрО10Ф1 (БрОФ10-1)
  • Bronze БрО10Ф0,7Н0,5 (БрОФН10-0,7-0,5)
  • Bronze БрО10С2Н3 (БрОСН10-2-3)
  • Bronze БрО10С10 (БрОС10-10)

    • Designation

    Name The value
    Designation GOST Cyrillic БрО10Ц2Н1,5
    Designation GOST Latin BpO10Ts2H1,5
    Transliteration BrO10Ts2N15
    By chemical elements BaSn10Zn2Ni1,5
    Name The value
    Designation GOST Cyrillic БрОЦН10-2-1,5
    Designation GOST Latin BpOTsH10-2-1,5
    Transliteration BrOTsN10-2-15
    By chemical elements BaSnZnNi10-2-1,5

    Description

    Bronze БрО10Ц2Н1,5 is used: for the manufacture of casting parts, metallurgical engineering (crowns worm wheels, large screws, responsible heavy-duty parts, anti-friction parts, fittings and other parts with a surface of the high purity).

    Note

    Vysokohromistyh bronze. Is a substitute of bronze stamps Bro5c5s5 (БрОЦС5−5-6) and Bra10zh3mc2 (Brazhmc10−3-1,5). The coefficient of friction of bronze without lubrication of 0.16 to 0.20, with grease — 0,008−0,060.

    Standards

    Name Code Standards
    Castings, non-ferrous metals and alloys В84 OST 24.916.01-71

    Chemical composition

    Standard S Si Ni Fe Cu Al Zn Sn Sb Pb Bi
    OST 24.916.01-71 ≤0.05 ≤0.02 1-2 ≤0.3 Rest ≤0.02 1-3 9-11 ≤0.5 ≤0.5 ≤0.005
    Cu is the basis.
    According to OST 24.916.01-71 the total content of impurities should be ≤ 1.00%.

    Mechanical properties

    σU, MPa d HB, MPa
    Castings are supplied without heat treatment
    ≥216 ≥6 ≥75
    ≥157 ≥3 ≥75

    Description mechanical marks

    Name Description
    σU Limit short-term strength
    d Elongation after rupture
    HB Brinell hardness number