Designation
| Name |
The value |
| Designation GOST Cyrillic |
01Х18М2Т |
| Designation GOST Latin |
01X18M2T |
| Transliteration |
01H18M2T |
| By chemical elements |
01Cr18Mo2Ti |
| Name |
The value |
| Designation GOST Cyrillic |
ЧС77 |
| Designation GOST Latin |
ChC77 |
| Transliteration |
ChS77 |
| By chemical elements |
ZrС77 |
Description
01Х18М2Т steel is used: for the manufacture of tubes in heat exchangers petrochemical equipment; parts of equipment persistent in the production of caustic soda, horsterweg environments, equipment of oil-refining and pulp industry with temperatures of up to +300 °C; the welding wire.
Standards
| Name |
Code |
Standards |
| Blanks. Of the workpiece. Slabs |
В31 |
TU 14-1-3547-83 |
| Sheets and strips |
В33 |
TU 14-1-3622-83 |
| Welding and cutting metals. Soldering, riveting |
В05 |
TU 14-1-3996-85 |
| Steel pipes and fittings to them |
В62 |
TU 14-3-1275-83 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Cu |
N |
Ti |
Mo |
| TU 14-1-3547-83 |
≤0.01 |
≤0.015 |
≤0.015 |
≤0.7 |
17-19 |
≤0.5 |
≤0.4 |
Rest |
≤0.15 |
≤0.01 |
0.15-0.35 |
1.8-2.5 |
Fe is the basis.
According to TU 14-1-3547-83, the chemical composition is given for steel grade 01Х18М2Т-ВИ (ЧС77-ВИ).
Mechanical properties
| Section, mm |
sT|s0,2, MPa |
σU, MPa |
d5, % |
| Pipe seamless in the delivery state after quenching on the other 14-3-1275-83 (DH = 25-75 mm, wall 2-3 mm) |
|
≥215 |
≥392 |
≥25 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |