Steel АЦ38ХС
Designation
Description
АЦ38ХС steel is used: for the production of bars intended for the manufacture of automotive components by hot forming with subsequent machining.
Note
Calcium-containing steel of high machinability.
Standards
Chemical composition
Fe is the basis.
According to TU 14-1-3283-81 chemical analysis is given for steel grade AC38XS. In the designation of steel letters mean: A - automatic, C - calcium. Microalloying of calcium steel is carried out by silicocalcium and other calcium alloys at the rate of introduction of 0,030-0,090% of calcium into liquid metal. The mass fraction of calcium is not determined by chemical analysis. The presence of tungsten to 0.20%, molybdenum to 0.15%, titanium to 0.030% and vanadium to 0.050% is not a defect. In the finished bars, subject to the requirements of the technical specification, deviations in chemical composition are allowed: in carbon ± 0.010%, in manganese ± 0.020%, in silicon ± 0.050%, in chromium ± 0.050%, in nickel -0.050%, in sulfur and phosphorus + 0.0050% of each.
According to TU 14-1-3283-81 chemical analysis is given for steel grade AC38XS. In the designation of steel letters mean: A - automatic, C - calcium. Microalloying of calcium steel is carried out by silicocalcium and other calcium alloys at the rate of introduction of 0,030-0,090% of calcium into liquid metal. The mass fraction of calcium is not determined by chemical analysis. The presence of tungsten to 0.20%, molybdenum to 0.15%, titanium to 0.030% and vanadium to 0.050% is not a defect. In the finished bars, subject to the requirements of the technical specification, deviations in chemical composition are allowed: in carbon ± 0.010%, in manganese ± 0.020%, in silicon ± 0.050%, in chromium ± 0.050%, in nickel -0.050%, in sulfur and phosphorus + 0.0050% of each.