Steel 18Х2МФА (48ТС-3)

Designation

Name	The value
Name	The value
Designation GOST Cyrillic	18Х2МФА
Designation GOST Latin	18X2MFA
Transliteration	18H2MFA
By chemical elements	18Cr2MoV

Name	The value
Name	The value
Designation GOST Cyrillic	48ТС-3
Designation GOST Latin	48TC-3
Transliteration	48TS-3
By chemical elements	48TiС-3

Description

18Х2МФА steel is used: for the production of workpieces in the form of forgings, sheets, sheet blanks, the sheet of stamped blanks, Cavanaugh-rolled billets (slabs), used for products of machinery and vessels, working under pressure and within the jurisdiction of the Gosatomenergonadzor.

Standards

Name	Code	Standards
Name	Code	Standards
Blanks. Of the workpiece. Slabs	В31	TU 108.131-86

Chemical composition

Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Cu	As	V	Mo	Co
Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Cu	As	V	Mo	Co
TU 108.131-86	0.16-0.21	≤0.02	≤0.02	0.3-0.6	2.5-3	0.17-0.37	≤0.4	Rest	≤0.3	≤0.04	0.25-0.35	0.6-0.8	≤0.025

Fe is the basis.
According to TU 108.131-86, the chemical composition is given for steel grade 18X2MFA. In the chemical composition, deviations are allowed: carbon ± 0.010%, manganese, silicon, and vanadium ± 0.050% each, chromium ± 0.10%.

Mechanical properties

Section, mm	s_T\|s_0,2, MPa	σ_U, MPa	d₅, %	y, %	KCU, kJ/m²	HB, MPa
Section, mm	s_T\|s_0,2, MPa	σ_U, MPa	d₅, %	y, %	KCU, kJ/m²	HB, MPa
Billet heat-treated in the delivery condition on the other 108.131-86
160-400	≥430	540-735	≥14	≥50	≥490	187-229
160-400	≥390	≥490	≥14	≥50	-	-
160-400	≥430	540-735	≥14	≥50	≥490	187-229
160-400	≥390	≥490	≥14	≥50	-	-
160-400	≥530	635-835	≥13	≥50	≥490	207-225
160-400	≥490	≥550	≥12	≥45	-	-

Description mechanical marks

Name	Description
Name	Description
s_T\|s_0,2	Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σ_U	Limit short-term strength
d₅	Elongation after rupture
y	The relative narrowing
KCU	Toughness
HB	Brinell hardness number