Designation
| Name |
The value |
| Designation GOST Cyrillic |
12Х2МФА |
| Designation GOST Latin |
12X2MFA |
| Transliteration |
12H2MFA |
| By chemical elements |
12Cr2MoV |
| Name |
The value |
| Designation GOST Cyrillic |
48ТС-2 |
| Designation GOST Latin |
48TC-2 |
| Transliteration |
48TS-2 |
| By chemical elements |
48TiС-2 |
Description
12Х2МФА steel is used: for the production of workpieces in the form of forgings, sheets, sheet blanks, the sheet of stamped blanks, Cavanaugh-rolled billets (slabs), used for products of machinery and vessels, working under pressure and within the jurisdiction of the Gosatomenergonadzor.
Standards
| Name |
Code |
Standards |
| Blanks. Of the workpiece. Slabs |
В31 |
TU 108.131-86 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Cu |
As |
V |
Mo |
Co |
| TU 108.131-86 |
0.11-0.16 |
≤0.02 |
≤0.02 |
0.3-0.6 |
2-2.5 |
0.17-0.37 |
≤0.4 |
Rest |
≤0.3 |
≤0.04 |
0.25-0.35 |
0.6-0.8 |
≤0.025 |
Fe is the basis.
According to TU 108.131-86 the chemical composition is given for steel grade 12X2MFA. In the chemical composition, deviations are allowed: carbon ± 0.010%, manganese, silicon, and vanadium ± 0.050% each, chromium ± 0.10%.
Mechanical properties
| Section, mm |
sT|s0,2, MPa |
σU, MPa |
d5, % |
y, % |
KCU, kJ/m2 |
HB, MPa |
| Billet heat-treated in the delivery condition on the other 108.131-86 |
| ≤160 |
≥430 |
540-735 |
≥14 |
≥50 |
≥490 |
187-229 |
| ≤160 |
≥390 |
≥490 |
≥14 |
≥50 |
- |
- |
| ≤160 |
≥430 |
540-735 |
≥14 |
≥50 |
≥490 |
187-229 |
| ≤160 |
≥390 |
≥490 |
≥14 |
≥50 |
- |
- |
| ≤160 |
≥530 |
635-835 |
≥13 |
≥50 |
≥490 |
207-225 |
| ≤160 |
≥490 |
≥550 |
≥12 |
≥45 |
- |
- |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |
| y |
The relative narrowing |
| KCU |
Toughness |
| HB |
Brinell hardness number |