    • Designation

    Name The value
    Designation GOST Cyrillic ВНЖ-95
    Designation GOST Latin BHZh-95
    Transliteration VNG-95
    By chemical elements ВNiFe-95

    Description

    Alloy RP-95 is used: for the manufacture of parts of cylinders, sleeves, slozhnofigurnye workpieces with curved surfaces: rotors, gyroscopes, inertial masses, rationalwiki electrodes, hoppers shaped charges, biological protection from gamma radiation.

    Note

    Powder heavy tungsten-Nickel-iron alloy.

    Standards

    Name Code Standards
    Non-ferrous metals, including rare, and their alloys В51 TU 48-19-84-81

    Chemical composition

    Standard Ni Fe W
    TU 48-19-84-81 3.2-3.7 1.5-2 Rest
    W is the basis.
    According to TU 48-19-84-81, the mass fraction of the components is indicated for the preparation of the powder mixture and it is not subject to control on the products.

    Mechanical properties

    sT|s0,2, MPa σU, MPa d5, % KCU, kJ/m2
    The product of the powder sintered
    680-700 785-950 5.2-12 294-392

    Description mechanical marks

    Name Description
    sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
    σU Limit short-term strength
    d5 Elongation after rupture
    KCU Toughness

    Physical characteristics

    Temperature r, kg/m3
    20 17600-18100

    A description of the physical symbols

    Name Description
    r Density
    l Coefficient of thermal conductivity
    R UD. the resistivity

    Technological properties

    Name The value
    Microstructure The microstructure of the alloy to be biphasic, consisting of a solid solution based on tungsten and a matrix consisting of a solid solution based on Nickel and iron.
    Particularities of production of goods Details of the alloy produced by powder metallurgy method, including hydrostatic extrusion, sintering (impregnation) in the environment of hydrogen and vacuum annealing. In the process of being sintered at 1350-1500 °C in the presence of a liquid phase occurs recrystallization of the tungsten powder with the formation of nearly spherical particles, ten times greater than the particle size of initial powder.