Designation
| Name |
The value |
| Designation GOST Cyrillic |
Х13Ю4 |
| Designation GOST Latin |
X13Ju4 |
| Transliteration |
H13Yu4 |
| By chemical elements |
Cr13Al4 |
| Name |
The value |
| Designation GOST Cyrillic |
ЭИ60 |
| Designation GOST Latin |
EI60 |
| Transliteration |
EhI60 |
| By chemical elements |
- |
Description
Alloy Х13Ю4 applies: for production of wire and tape resistors, heating elements of domestic appliances and apparatus; resistance elements.
Note
The heat resisting alloy in an oxidizing atmosphere.
Standards
| Name |
Code |
Standards |
| Tape |
В34 |
GOST 12766-67 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Al |
Ti |
Zr |
| GOST 12766-67 |
≤0.15 |
≤0.025 |
≤0.035 |
≤0.7 |
12-15 |
≤1 |
≤0.6 |
Rest |
3.5-5.5 |
≤0.3 |
≤0.5 |
Fe is the basis.
According to GOST 12766-67 the chemical composition is given for the alloy grade X13S04. The presence in the alloy of residual rare-earth elements, as well as barium and calcium, is not a defective feature.
Physical characteristics
| Temperature |
r, kg/m3 |
R, Mr. · m |
| 20 |
7300 |
1180-1340 |
A description of the physical symbols
| Name |
Description |
| r |
Density |
| R |
UD. the resistivity |
Technological properties
| Name |
The value |
| Microstructure |
Ferritic structure. |
| Magnitnoi |
Magnetic alloy. |
| Okalinolomatel, heat resistance |
Onlinetony alloy in an oxidizing atmosphere and in the atmosphere containing sulfur and sulfur compounds; is prone to sagging at high temperatures. |
| Operating temperature |
The working temperature of heating element: Optimal 900 °C, maximum 1000 °C. |