    • Designation

    Name The value
    Designation GOST Cyrillic АСМ
    Designation GOST Latin ACM
    Transliteration ASM
    By chemical elements -

    Description

    Alloy ASM is used: for bimetallic strip steel by rolling and subsequent punching of liners with a thickness of friction layer is less than 0.5 mm.

    Note

    The recommended modes of operation:
    — load ≤ 19,5 Mn/m2 (200 kg/cm2);
    — sliding speed ≤ 10 m/s;
    — temperature ≤ 100 °C;
    — recommended shaft hardness ≥ 250 HB.
    On an antifriction layer of articles coated with a soft metal or a polymer antifriction coating thickness of from 0.003 to 0.03 mm. permitted by agreement with the consumer in technically justified cases to cover the product with a soft metal or polymer coating.

    Standards

    Name Code Standards
    Non-ferrous metals, including rare, and their alloys В51 GOST 14113-78
    Sheets and strips В53 TU 48-21-670-79, TU 48-21-83-83

    Chemical composition

    Standard Mn Si Fe Cu Al Zn Sb Mg
    GOST 14113-78 ≤0.2 ≤0.5 ≤0.75 ≤0.1 Rest ≤0.1 3.5-6.5 0.3-0.7
    Al is the base.
    According to GOST 14113-78, the content of other impurities, individually, should be ≤ 0.050%, and the total content of other impurities should be ≤ 0.10%.

    Mechanical properties

    Section, mm sT|s0,2, MPa σU, MPa d5, % y, % HB, MPa
    Casting in a metal mold in the state of delivery
    32-46 85-95 30-38 45-52 22-30

    Description mechanical marks

    Name Description
    sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
    σU Limit short-term strength
    d5 Elongation after rupture
    y The relative narrowing
    HB Brinell hardness number