    • Designation

    Name The value
    Designation GOST Cyrillic М3
    Designation GOST Latin M3
    Transliteration M3
    By chemical elements Cu3

    Description

    Copper M3 is used: for the production of rolled alloys copper-based and other casting alloys; for the manufacture of products of cryogenic equipment; round drawn thin-walled tubes; drawn rectangular tubes, intended for the manufacture of waveguides; cold-rolled foil and strip, cold-rolled and hot-rolled sheets and plates of General purpose; radiator tape, is intended for manufacturing cooling tubes and radiator fins; drawn capillary tubes used in propose hypersound or ultras and instrumentation and refrigeration equipment.

    Note

    M3 copper produced by fire refining and smelting waste and scrap of copper.

    Standards

    Name Code Standards
    Tape В54 GOST 1018-77, GOST 20707-80, GOST 1173-2006, GOST Р 50248-92, OST 4.021.077-92
    Bars В55 GOST 1535-2006, OST 4.021.019-92
    Tubes of non-ferrous metals and alloys В64 GOST 2624-77, GOST 11383-75, GOST 20900-75, GOST 617-2006, OST 4.021.122-92
    Sheets and strips В53 GOST 495-92, OST 4.021.049-92
    Non-ferrous metals, including rare, and their alloys В51 GOST 859-2001, OST 4.021.009-92

    Chemical composition

    Standard S Ni Fe Cu As Sn Sb Pb Bi O
    GOST 1018-77 ≤0.01 ≤0.2 ≤0.05 Rest ≤0.01 0.02-0.05 ≤0.05 ≤0.05 ≤0.003 ≤0.08
    GOST 1173-2006 ≤0.01 ≤0.2 ≤0.05 Rest ≤0.01 ≤0.05 ≤0.05 ≤0.05 ≤0.003 ≤0.08
    Cu is the basis.
    According to GOST 1173-2006, GOST 1535-2006 and GOST 859-2001 the total content of Cu + Ag is ≥ 99.50%.

    Mechanical properties

    Section, mm σU, MPa d5, % d d10 HB, MPa HV, MPa
    The tape is supplied according to GOST 1018-77 (samples)
    0.35-1.86 ≥200 - ≥36 - - -
    Cold-rolled steel strip of 0.05-2.0 mm in the delivery state on the EAST 4.021.077-92 (samples transverse)
    - 200-260 - ≥36 - - -
    - ≥290 - ≥3 - - -
    Ribbons and leaves (≥0.5 mm) as supplied
    - ≥200 - - ≥30 - -
    - 200-260 ≥45 - ≥36 ≥55 40-65
    - 240-310 ≥15 - ≥12 ≥75 65-95
    - ≥290 ≥6 - ≥3 ≥95 90-110
    Sheet metal as supplied at OST 4.021.049-92 (samples transverse)
    0.4-10 20-260 - - ≥36 ≥55 -
    0.4-10 ≥290 - - ≥3 ≥95 -
    Bars at the EAST 4.021.019-92, GOST 1535-2006 in the delivery condition (longitudinal samples)
    - ≥190 ≥35 - ≥20 ≥35 ≥40
    - ≥200 ≥40 - ≥35 ≥40 40-65
    - ≥240 ≥15 - ≥10 ≥60 70-95
    - ≥270 ≥8 - ≥5 ≥70 90-115
    The pulled capillary tube in the state of delivery according to GOST 2624-77 (samples)
    - ≥200 ≥40 - ≥35 - -
    - ≥250 ≥5 - ≥4 - -
    Pipe humanitariannet and extruded in the state of delivery according to GOST 617-2006 (in cross-section is specified outside diameter, in brackets are the values for pipes with improved plasticity and strength)
    ≤360 ≥200 (210) ≥38 - ≥35 (40) - ≤55
    ≤360 ≥240 (270) ≥10 - ≥8 (8) - -
    ≤200 ≥190 ≥32 - ≥30 - ≤80
    200 ≥180 ≥32 - ≥30 - -
    ≤360 ≥280 (310) - - - - 90-135

    Description mechanical marks

    Name Description
    σU Limit short-term strength
    d5 Elongation after rupture
    d Elongation after rupture
    d10 Elongation after rupture
    HB Brinell hardness number
    HV The Vickers hardness

    Physical characteristics

    Temperature Е, HPa r, kg/m3 l, W/(m · °C) R, Mr. · m С, J/(kg · °C)
    20 132 8940 387 178 390

    A description of the physical symbols

    Name Description
    Е The normal elasticity modulus
    l Coefficient of thermal conductivity
    R UD. the resistivity
    С Specific heat