Brass Lc37mc2s2k

  • Brass LSdh
  • Brass ЛЦ40Сd (ЛС59-1ЛД)
  • Brass LC40S (LS59-1L)
  • Brass ЛЦ40Мц3Ж (ЛМцЖ55-3-1)
  • Brass ЛЦ40Мц3А
  • Brass ЛЦ40Мц1,5 (ЛМц58-2L)
  • Brass LC40AJ
  • Brass ЛЦ38Мц2С2
  • Brass ЛЦ37Мц2С2К
  • Brass LC30A3 (LA67-2,5)
  • Brass ЛЦ25С2
  • Brass LC23A6Zh3Mz2
  • Brass ЛЦ16К4 (ЛК80-3L)
  • Brass ЛЦ14К3С3
  • Brass LC10 (L90L)
  • Brass LSch
  • LSd brass
  • LS Brass
  • Brass VOC
  • Brass LMZSCA
  • Brass LMZSC
  • Brass LMZS (LMZS58-2-2)
  • Brass LMZKA
  • Brass LMZh
  • LKS Brass
  • Brass LK2
  • Brass LK1
  • Brass LC
  • Brass LAMZ (LAMZ66-6-3-2)
  • Brass LA

    • Designation

    Name The value
    Designation GOST Cyrillic ЛЦ37Мц2С2К
    Designation GOST Latin LTs37Mts2C2K
    Transliteration LTs37Mts2S2K
    By chemical elements ЛZn37Mn2Pb2

    Description

    Brass Lc37mc2s2k used: for the manufacture of anti-friction casting parts, valves.

    Note

    Brass manganese-lead-silicon.

    Standards

    Name Code Standards
    Non-ferrous metals, including rare, and their alloys В51 GOST 17711-93, GOST Р 50425-92

    Chemical composition

    Standard P Mn Si Ni Fe Cu As Al Zn Sn Sb Pb Bi
    GOST 17711-93 ≤0.1 1.5-2.5 0.5-1.3 ≤1 ≤0.7 57-60 ≤0.05 ≤0.7 Rest ≤0.6 ≤0.1 1.5-3 ≤0.01
    Zn is the basis.
    According to GOST 17711-93 the total share of impurities should be ≤ 1.7%. Impurities not specified are taken into account in the total amount of impurities. The mass fraction of nickel in brass is allowed at the expense of copper and is not included in the sum of impurities.

    Mechanical properties

    σU, MPa d5, % HB, MPa
    Castings on OST 1 90077-72
    ≥343 ≥2 ≥110

    Description mechanical marks

    Name Description
    σU Limit short-term strength
    d5 Elongation after rupture
    HB Brinell hardness number