Marking
The marking of the high-speed steels, which are produced according to the technical standards
Chemical composition of high-speed steels (GOST 19265-73)
| Steel grade | C | Cr | W | V | Co | Mo, not more |
| Р18 | 0,70-0,80 | 3,8-4,4 | 17,5-4,4 | 1,0-1,4 | - | 0,3 |
| Р12 | 0,80-0,90 | 3,1-3,6 | 12,0-13,0 | 1,5-1,9 | - | 0,3 |
| Р9 | 0,85-0,95 | 3,8-4,4 | 8,5-10,0 | 2,0-2,6 | - | 0,3 |
| Р6М3 | 0,85-0,95 | 3,0-3,6 | 5,5-6,5 | 2,0-2,5 | - | 3,0-3,6 |
| R18F5 | 0,85-0,95 | 3,8-4,4 | 17,5-19,0 | 1,8-2,4 | - | 0,5 |
| P9F5 | 1,40-1,50 | 3,8-4,4 | 9,0-10,5 | 4,3-5,1 | - | 0,4 |
| R14F4 | 1,20-1,30 | 4,0-4,6 | 13,0-14,5 | 3,4-4,1 | - | 0,4 |
| P9K5 | 0,90-1,00 | 3,8-4,4 | 9,0-10,5 | 2,0-2,6 | 5,0-6,0 | 0,3 |
| Р9К10 | 0,90-1,00 | 3,8-4,4 | 9,0-10,5 | 2,0-2,6 | 9,5-10,5 | 0,3 |
| R10K5F5 | 1,45-1,55 | 4,0-4,6 | 10,0-11,5 | 4,3-5,1 | 5,0-6,0 | 0,3 |
| Р18К5Ф2 | 0,85-0,95 | 3,8-4,4 | 17,5-19,0 | 1,8-2,4 | 5,0-6,0 | 0,5 |
Notes1. The content of Mn, Si and Ni not more than 0,4%; S and P not more than 0,03% (for alloys R9F5, R14F4 and R10K5F5 allowed 0,035% P). 2. Tolibden content of up to 1% in steel R18 and up to 0,6% in steel R9 (grade R18M and R9M) is allowed. If the Mo content of P18M and P9M exceeds 0.3%, the W content may be reduced (1% Mo replaces 2% W). | ||||||
Evek GmbH offers to buy a wide range of fast-cutting steel at an affordable price. We provide delivery of products to any point on the continent. The price is optimal.
Classification
By its chemical composition, high speed steel is divided into tungsten (P9, P12, P18, P18F2), high-cobalt (P9F5, P14F4), cobalt (P9K5, P9K10) and cobalt vanadium (P10K5F5, P18K5F2). A number of steels which by their properties and application are referred to high speed steel are produced by customers' order and are not included into
| Steel grade | C | W | Mo | Cr | V | Co | Ti |
| P7T | 0,80 | 7,5 | - | 3,0 | 1,3 | - | 0,15 |
| R6M3K5F2 | 0,90 | 6,0 | 3 | 4,0 | 2,3 | 5,0 | - |
| P18K8F2M (EP 379) | 1,00 | 18,0 | 1 | 4,0 | 2,2 | 8,0 | - |
Range of the produced high-speed steels:
hot-rolled and forged bars - round and square, strips;
Round bars with enhanced surface finish and increased dimensional accuracy;
cold rolled strip.
Properties of high-speed steels in delivery condition
| Steel grade | density, kg/m³ |
As1, deg |
Ar1, deg |
Temperature in °C | Brinell hardness, NV | Weight percentage of carbide phase | |
| forging | annealing | ||||||
| Р18 | 8700 | 820 | 760 | 1200-900 | 840 | 207-255 | 28 |
| Р9 | 8300 | 810 | 760 | 1200-900 | 850 | 207-255 | 17 |
| Р12 | 8500 | 810 | 760 | 1200-900 | 840 | 207-255 | 23 |
| R18F2 | 8700 | 820 | 760 | 1200-900 | 840 | 207-269 | 27 |
| R9F5 | 8110 | - | - | 1180-900 | 850 | 207-269 | 20 |
| R14F4 | 8420 | - | - | 1180-900 | 850 | 207-269 | 22 |
| R9K5 | 8300 | - | - | 1150-900 | 850 | 207-269 | 17 |
| R9K10 | 8300 | - | - | 1180-900 | 850 | 207-269 | 16 |
| R10K5F5 | 8130 | - | - | 1180-900 | 850 | 207-269 | 22 |
| R18K5F2 | 8200 | - | - | 1200-900 | 850 | 285 | 25 |
| R6M5 | 8500 | - | - | 1150-900 | 840 | 207-235 | 20 |
| Р18К8Ф2М | 8700 | 820 | - | 1180-900 | 860 | 262-270 | - |
| Note. Cooling after annealing is carried out with the furnace at a rate not exceeding 30 0 C / s | |||||||