Steel У11А (11)
Designation
Description
У11А steel is used: for the manufacture of hand taps, rasps, needle files, saws for wood processing, matrices for cold forming, axes, gauges simple form and low accuracy classes.
Standards
Chemical composition
Fe is the basis.
According to GOST 1435-90 the mass fraction of chromium, nickel and copper is indicated for 1 group of metal products. The mass fraction of sulfur in steel obtained by the electroslag remelting method should not exceed 0.013%. In the metal products of the 2nd group, the mass fraction of Cr ≤ 0.12%, Ni ≤ 0.12%, Cu ≤0.20% and their total mass fraction ≤ 0.40%. In the metal products of the third group, the mass fraction of Cr ≤ 0.20-0.40%, Ni ≤ 0.25%, Cu ≤0.25%. In metal products of the 1 st and 3 rd groups, made of steel obtained by scrap-process, the mass fractions of nickel, copper and chromium are increased by 0.05% of each element as compared to those in the table. In a metal designed for the manufacture of cold-rolled strip, an increase in the mass fraction of nickel, copper and chromium is not allowed.
According to TU 14-1-505-73, by agreement of the parties for special purpose hardware, steel should be supplied with reduced content limits of elements without treatment with synthetic slag and purging with argon.
According to GOST 1435-90 the mass fraction of chromium, nickel and copper is indicated for 1 group of metal products. The mass fraction of sulfur in steel obtained by the electroslag remelting method should not exceed 0.013%. In the metal products of the 2nd group, the mass fraction of Cr ≤ 0.12%, Ni ≤ 0.12%, Cu ≤0.20% and their total mass fraction ≤ 0.40%. In the metal products of the third group, the mass fraction of Cr ≤ 0.20-0.40%, Ni ≤ 0.25%, Cu ≤0.25%. In metal products of the 1 st and 3 rd groups, made of steel obtained by scrap-process, the mass fractions of nickel, copper and chromium are increased by 0.05% of each element as compared to those in the table. In a metal designed for the manufacture of cold-rolled strip, an increase in the mass fraction of nickel, copper and chromium is not allowed.
According to TU 14-1-505-73, by agreement of the parties for special purpose hardware, steel should be supplied with reduced content limits of elements without treatment with synthetic slag and purging with argon.