Steel 60S2N2A

Designation

Name	The value
Designation GOST Cyrillic	60С2Н2А
Designation GOST Latin	60C2H2A
Transliteration	60S2N2A
By chemical elements	60С2Н2

Description

60S2N2A steel is used: for the production of responsible and heavy-duty springs and leaf springs.

Note

Steel spring alloy of high quality.

Standards

Name	Code	Standards
Sheets and strips	В23	GOST 103-2006
Bars and shapes	В22	GOST 1133-71, GOST 2590-2006, GOST 2591-2006, GOST 2879-2006
Steel wire medium and high carbon	В72	GOST 26366-84
Sheets and strips	В33	GOST 4405-75, TU 14-1-723-73
Bars and shapes	В32	GOST 7417-75, GOST 7419-90, GOST 8559-75, GOST 8560-78, GOST 14955-77, GOST 14959-79, TU 14-1-2118-77, TU 14-11-245-88, TU 14-136-367-2008

Chemical composition

Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Cu
GOST 14959-79	0.56-0.64	≤0.025	≤0.025	0.4-0.7	≤0.3	1.4-1.8	1.4-1.7	Rest	≤0.2

Fe is the basis.

Mechanical properties

Section, mm	t отпуска, °C	s_T\|s_0,2, MPa	σ_U, MPa	d₅, %	d₄	y, %	HB, MPa
Rolled sheet. Annealing at 720 °C, cooling with the furnace
≤3.9	-	≤410	≤700	-	≥19	≥50	-
Rolled steel. Quenching in oil from 870 °C to + Vacation
-	380	≥1780	≥1920	≥6	-	≥40	-
-	400	≥1690	≥1760	≥6	-	≥41	-
Spring. Annealing or leave before the drawing at 730 °C, hot coiling at 850-900 °C + Quenching in oil with 850-870 °C + Vacation at 380-420 °C, air cooling
-	-	-	-	-	-	-	420-475
Rolled steel. Quenching in oil from 850 °C + Vacation at 420 °C, air cooling
10-25	-	≥1570	≥1710	≥5	-	≥20	-
Rolled steel. Quenching in oil from 870 °C to + Vacation
-	420	≥1530	≥1640	≥7	-	≥41	-
Rolled steel. Steel categories: 3, 3A, 3B, 3C, 3D, 4, 4A, 4B. Quenching in oil from 870 °C to + vacation at 470 °C
	-	≥1325	≥1470	≥8	-	≥30	-
Rolled steel. Quenching in oil from 870 °C to + Vacation
-	440	≥1390	≥1490	≥8	-	≥42	-
-	460	≥1360	≥1440	≥8	-	≥41	-
-	480	≥1230	≥1340	≥9	-	≥40	-
-	500	≥1210	≥1300	≥10	-	≥41	-
-	520	≥1100	≥1170	≥12	-	≥43	-

Description mechanical marks

Name	Description
s_T\|s_0,2	Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σ_U	Limit short-term strength
d₅	Elongation after rupture
d₄	Elongation after rupture
y	The relative narrowing
HB	Brinell hardness number

Physical characteristics

Temperature	Е, HPa	G, HPa
0	191	78

A description of the physical symbols

Name	Description
Е	The normal elasticity modulus
G	Modulus of elasticity shear torsion
r	Density
l	Coefficient of thermal conductivity
R	UD. the resistivity
a	The coefficient of linear expansion

Technological properties

Name	The value
Weldability	does not apply to welded structures.
Склонность к отпускной хрупкости	tend not
The temperature of forging	Start - 1150 °C, the end - 850 °C.
Flock-sensitive sensitivity	sensitive