Steel 60ХФА (60ХФ)

Designation

Name	The value
Designation GOST Cyrillic	60ХФА
Designation GOST Latin	60XFA
Transliteration	60HFA
By chemical elements	60CrV

Name	The value
Designation GOST Cyrillic	60ХФ
Designation GOST Latin	60XF
Transliteration	60HF
By chemical elements	60CrV

Description

60ХФА steel is used: for the manufacture of heavy-duty parts with high fatigue strength; springs operating at temperatures to +200 °C; the tool.

Note

Steel spring, chrome vanadium high quality instrumental belongs to the group of presintering steels.

Standards

Name	Code	Standards
Bars and shapes	В32	TU 14-1-1547-75, TU 14-1-462-72
Blanks. Of the workpiece. Slabs	В31	TU 14-1-1842-76

Chemical composition

Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Cu	V
TU 14-1-1842-76	0.55-0.65	≤0.03	≤0.03	0.5-0.8	0.8-1.1	0.17-0.37	≤0.3	Rest	-	0.1-0.2
TU 14-1-462-72	0.55-0.65	≤0.025	≤0.025	0.5-0.8	0.8-1.1	0.17-0.37	≤0.25	Rest	≤0.2	0.1-0.2

Fe is the basis.
According to TU 14-1-1842-76 the chemical composition is given for steel grade 60HFA. The permissible deviations in chemical composition are in accordance with GOST 14959.
According to TU 14-1-462-72 the chemical composition is given for steel grade 60HFA. The permissible deviations in chemical composition are in accordance with GOST 4543.

Technological properties

Name	The value
Macrostructure and pollution	The macrostructure of the square billets on the other 14-1-1842-76 in fractures treated or templete should not have shrinkage, porosity, bubbles, delaminations, cracks, inclusions and placenow.
Particularities of production of goods	Billets, on the other 14-1-1842-76 supplied in the annealed condition.
Machinability	Hard cutting. Requires the use of cutters made of special materials, such as, carbide inserts brand T15K6. Optimal cutting conditions: cutting speed v = 65 mm/min; feed s = 0.12 mm/Rev wet (emulsion).