Alloy SV-08Х25Н60М10 (ЭП606)

  • Alloy PANCH-11
  • Alloy Sv-03H20N45G6M6B (EP953)
  • Alloy Св-08Х20Н57М8В8Т3Р (EP533)
  • Alloy Sv-08X25N25M3 (EP622)
  • Alloy Sv-08Х25Н40М7 (EP673)
  • Alloy Sv-08Х25Н60М10 (EP606)
  • Alloy Sv-36NGMT (EP803)
  • Alloy SvHN60MVU (ChS40)

    • Designation

    Name The value
    Designation GOST Cyrillic Св-08Х25Н60М10
    Designation GOST Latin Cb-08X25H60M10
    Transliteration Sv-08H25N60M10
    By chemical elements 08Cr25Ni60Cu10
    Name The value
    Designation GOST Cyrillic ЭП606
    Designation GOST Latin EP606
    Transliteration EhP606
    By chemical elements -

    Description

    Alloy SV-08Х25Н60М10 used: for the production of welding wire designed for mechanized welding of dissimilar heat-resistant steels with high-alloy heat-resistant steels and welding of hardened steels without subsequent heat treatment in construction, metallurgy, oil extraction, medicine, heavy engineering, operating in the temperature range 550−600 °C; the manufacture of electrodes ANZHR-1.

    Note

    High-alloyed high-temperature Nickel-based alloy.

    Standards

    Name Code Standards
    Welding and cutting metals. Soldering, riveting В05 TU 14-1-4968-91, TU 14-4-568-74, TU 14-1-773-73, TU 14-1-2461-78

    Chemical composition

    Standard C S P Mn Cr Si Ni Fe Ti Mo
    TU 14-1-4968-91 ≤0.1 ≤0.015 ≤0.015 1-2 23.5-26.5 ≤0.4 58.5-61.5 Rest - 9-11
    TU 14-4-568-74 ≤0.11 ≤0.016 ≤0.023 1.4-2.6 22-26 ≤0.4 57-61.5 Rest ≤0.1 8.8-11
    Ni is the basis.
    According to TU 14-1-4968-91, the chemical composition is given for the alloy Sv-08X25N60M10 (EP606).
    According to TU 14-4-568-74, the chemical composition is given for the welded weld metal made by the ANZhR-1 welding electrode manufactured from the Sv-08Kh25N60M10 alloy (EP606).

    Mechanical properties

    σU, MPa d5, % KCU, kJ/m2
    Weld, the weld electrode brand ANZHR-1 in the initial state on the other 14-4-568-74
    ≥610 ≥25 ≥1177

    Description mechanical marks

    Name Description
    σU Limit short-term strength
    d5 Elongation after rupture
    KCU Toughness

    Technological properties

    Name The value
    Microstructure The content of ferritic phase in the wire is governed only by agreement of the parties.
    Particularities of production of goods Wire on the other 14-1-4968-91 diameter up to 2.0 mm inclusively, supplied in cold-worked condition with a compression no more than 50% and over 2.0 mm supplied in heat treated condition.