Alloy ХН57КВЮТМБРЛ (ЧС88У)

Designation

Name	The value
Designation GOST Cyrillic	ХН57КВЮТМБРЛ
Designation GOST Latin	XH57KBJuTMBPL
Transliteration	HN57KVYuTMBRL
By chemical elements	CrNi57CoВAlTeCuBeHg

Name	The value
Designation GOST Cyrillic	ЧС88У
Designation GOST Latin	ChC88U
Transliteration	ChS88U
By chemical elements	ЧPb88У

Description

Alloy ХН57КВЮТМБРЛ used: for the production of cast bars in a vacuum-induction remelting for the manufacture by the method of directional solidification of shaped castings of parts of power engineering, operating at temperatures up to 1150 °C.

Note

High-temperature Nickel-based alloy with hafnium.

Standards

Name	Code	Standards
Bars and shapes	В32	TU 14-1-4828-90

Chemical composition

Standard	C	S	P	Mn	Cr	Si	Ni	Fe	Cu	N	As	Al	B	Ti	Mo	Sb	Pb	Bi	Nb	W	Ce	Zr	Co	Y	Hf
TU 14-1-4828-90	0.04-0.09	≤0.008	≤0.008	≤0.3	15.4-16.3	≤0.3	Rest	≤0.9	≤0.1	≤0.01	≤0.0005	2.8-3.3	0.06-0.1	4.2-5	1.6-2.3	≤0.0005	≤1.0E-5	≤5.0E-5	0.1-0.3	4.7-5.9	0.015	0.05	10-11.5	0.03	0.2-0.4

Ni is the basis.
According to TU 14-1-4828-90 the chemical composition is given for the alloy KhN57KVYUTMBLL-VI (ChS88U-VI). Zirconium, yttrium and cerium are introduced into the metal by calculation and chemical analysis are not determined. It is possible to estimate the mass fraction of arsenic in points on the scale of spectral analysis - the mass fraction of arsenic should be no more than 1 point.

Technological properties

Name	The value
Particularities of production of goods	Cast bars on the other 14-1-4828-90 are supplied with a diameter of 95 mm with a solid abrasive Stripping. On the surface of bars allowed in: oxide films, contamination, inclusion of foreign metal as well as afloat, increasing the size of bars. Quality control of the surface subjected to each rod according to agreed standards.