Sheet, strip 15x5m - 1.7362 - aisi 501
International Equivalent
| Mark | Analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| 15Х5М | H5M | 1.7362 | 501 | X12CrMo5 | Delivery from the stock, in stock |
Supplier
Buy a sheet, tape 15x5m — 1.7362 — aisi 501 from the supplier’s stock Evek GmbH. Full compliance with the international quality standards. Supplier Evek GmbH offers to buy a sheet, tape 15x5m (H5M) — aisi 501, the optimal price today.
Technical characteristics
Stainless steel heat-resistant low alloy steel of the martensitic class. The basis of the alloy — iron: its share of about 92%. Composition alloyed with chromium, Nickel, vanadium, tungsten, manganese, titanium, copper,. Used in the production of pipes, pipe fittings, valves, fasteners and similar parts operating at t° to 600 °C; the Term of work more than 10000 hours. Temperature an intensive formation of oxides of 650 °C ;
Percentage composition GOST 20072−74
| Fe | C | Si | Mn | Ni | S | P | Cr | Mo | W | V | Ti | Cu |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| basis | ≤0.15 | ≤0.5 | ≤0.5 | ≤0.6 | ≤0.025 | ≤0.03 | 4.5 — 6 | 0.45 — 0.6 | ≤0.3 | ≤0.05 | ≤0.03 | ≤0.2 |
Hardness (after heat treatment) 10−1 HB 170 — 217 MPa. The tendency to temper brittleness:
Mechanical properties (t° 20°C)
| Assortment | GOST | Eg. | sin | sT | d5 | y | KCU | Heat treatment |
|---|---|---|---|---|---|---|---|---|
| - | mm | MPa | MPa | % | % | kJ / m2 | - | |
| Tube hot | 550−75 | 392 | 216 | 22 | 50 | 1180 | ||
| Bars | 20072−74 |
Ø 90 | 390 | 215 | 22 | 50 | 1180 | Annealing 840 — 860 °C Cooling furnace |
| The leaves are thick | 7350−77 | 470 | 235 | 18 | Annealing 840 — 870 °C, Cooling air, |
Physical properties
| t° | E 10— 5 | a 10 6 | l | weight share | C | R 10 9 |
|---|---|---|---|---|---|---|
| Degree | N/mm2 | 1/Degree | W/(m·deg) | GS/m3 | J/(kg·deg) | Ohm·m |
| 20 | 2.11 | 7,75 | 430 | |||
| 100 | 11.3 | 37 | 7,73 | 483 | ||
| 400 | 1.78 | 12.2 | 34 | 7,64 | ||
| 600 | 1.02 | 12.5 | 32 | 7,58 |
sin the Limit of short-term strength
sT — the Limit of proportionality (yield strength for permanent deformation)
d5 — elongation at break
HB — Hardness Brinell
E — the Modulus of elasticity of the first kind
C — specific heat capacity
Analogues
| The European Union | Germany | Italy | China | Poland | USA | France | Czech Republic |
|---|---|---|---|---|---|---|---|
| EN | DIN, WNr | UNI | GB | PN | AFNOR | CSN | |
| 1.7362 | 1.7362 | A16CrMo25−5KG |
10MoCr50 | H5M | 501 | 710CD5−05 | 17102 |
| 5CrMo16 | 12CrMo19−5 |
A16CrMo25−5KW | 502 | Z15CD5−05 | |||
| T5 |
K41545 | Z20CD5 | |||||
| X12CrMo5 | X12CrMo5 |
S50100 | |||||
| S50200 | |||||||
| T12005 | |||||||
| T51605 |