Wire, circle, rod 2.0940 - CuAl10Fe - C95200
International Equivalent
| Mark | Analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| 2.0940 | C95200 | CuAl10Fe2-C | Delivery from the stock, in stock |
Buy, supplier
Buy bronze wire, rounds, bars C95200, 2.0940, CuAl10Fe from the supplier Evek GmbH at an affordable price. The price of nonferrous rolled steel is formed on the basis of European standards of production. Buy bronze wire, rounds, bars brand 2.0940, CuAl10Fe at an affordable price you can wholesale or retail. Regular customers can take advantage of a discount system from the company Evek GmbH.
Technical characteristics
Aluminum bronze is the highest-strength copper-based alloy. All aluminum bronzes can be heat treated, which further increases the tensile strength.
Percentage composition according to ASTM B505
| Cu | Al | Fe | Impurities |
|---|---|---|---|
| base | 8,5-9,5 | 2.5-4.5 | ≤ 0.05 |
Copper content at least 86%.This alloy is a very resistant bronze with excellent corrosion resistance, good electrical conductivity, wear resistance and impact resistance. The alloy withstands high pressure and has good antifriction characteristics, but its machinability is difficult.
A similar specification is
| CDA | ASTM | SAE | Federal | Military | Other |
|---|---|---|---|---|---|
| C95200 | B505 | 68A J461 J462 |
QQ-C-390, G6; QQ-B-671, CLASS 1 |
MIL-B-16033, CLASS 1 | ALUMINUM BRONZE 9A |
Mechanical Properties at 20 °C (ASTM B505/B505M-14)
| Minimum tensile strength | Yield strength (at 0.5% elongation under minimum load) | Elongation (at 2 or 50 mm, min,%) | Elongation (at 2 or 50 mm, min, %), % Extension (at 2 or 50 mm, min) | Brinell hardness (min) |
|---|---|---|---|---|
| Ksi | MPa | Ksi | MPa | |
| 68 | 469 | 26 | 179 | 20 |