Н65Д29ЮТ alloy (K-Monel)

  • Alloy H60MFL
  • Alloy H65D29YuT (K-Monel)
  • Alloy H65M (EP982)
  • Alloy H65MFL
  • Alloy H70MFV (EP814A)
  • Alloy KhN50MD (EP963)
  • Alloy KhN58V (EP795)
  • Alloy CrN63MB (EP758U; CrN60MB)
  • Alloy CrN65MV (EP567)
  • Alloy CrN65MVU (EP760)
  • Alloy KhN68BMYUVC (LZh-1)

    • Designation

    Name The value
    Designation GOST Cyrillic Н65Д29ЮТ
    Designation GOST Latin H65D29JuT
    Transliteration N65D29YuT
    By chemical elements Ni65Д29AlTe
    Name The value
    Designation GOST Cyrillic К-Монель
    Designation GOST Latin K-Mohel
    Transliteration K-Monel
    By chemical elements Co-Cuонель

    Description

    Alloy Н65Д29ЮТ used: for manufacturing of details of pumps and increased corrosion resistance; the shafts of modules, sections and input units of submersible centrifugal pumps; shafts of submersible centrifugal pumps, ECNC for oil.

    Standards

    Name Code Standards
    Blanks. Of the workpiece. Slabs В31 TU 14-1-3833-84
    Bars and shapes В32 TU 14-1-3917-85

    Chemical composition

    Standard C S P Mn Si Ni Fe Cu Al Ti
    TU 14-1-3917-85 0.1-0.2 ≤0.005 ≤0.008 0.5-1 0.1-0.5 Rest 0.9-1.5 27.5-30 2-4 0.25-1
    Ni is the basis.
    According to TU 14-1-3917-85 and TU 14-1-3833-84, the chemical composition is presented for the alloy N65D29YUT-ISH (K-monel) of vacuum induction smelting with subsequent electroslag remelting.

    Mechanical properties

    sT|s0,2, MPa σU, MPa d
    The billet is hot rolled in the state of delivery on the other 14-1-3833-84. Quenching in water technology manufacturer
    245-588 587-833 ≥30
    The grooved bars as supplied on the other 14-1-3917-85. Aging at 620±10 °C (delay of 6-10 h), air cooling
    ≥880 ≥980 ≥11

    Description mechanical marks

    Name Description
    sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
    σU Limit short-term strength
    d Elongation after rupture

    Technological properties

    Name The value
    Storage Bars on the other 14-1-3917-85 are supplied without grease, wrapped in synthetic film and Packed in returnable metal containers, made by the user. The total mass of bars in a bundle not more than 1 ton is permitted by an agreement with the consumer metal packaging in returnable containers a few of the ligament weight not exceeding 5 tonnes (gross). Storage of packaged bars are made in closed rooms with natural ventilation at temperatures from -60 °C to +50 °C without direct exposure to moisture. Storage and intrashop transportation of bundles and uncompressed bars must be carried out without damage.