    • Designation

    Name The value
    Designation GOST Cyrillic МА2-1пч
    Designation GOST Latin MA2-1pch
    Transliteration MA2-1pch
    By chemical elements CuAl2-1пч

    Description

    Alloy MA2−1pch used: for the manufacture of semi-finished products (sheets, plates, rods, sheets, tubes, wire, stampings and forgings) by hot deformation; extruded sections with cross sectional area up to 12 cm2 and a diameter of the circumscribed circle of up to 150 mm; ingots and slabs intended for the production of panels, stampings complex configuration for welding constructions with maximum operating temperatures up to +150 °C — long, up to +200 °C — short-term.

    Standards

    Name Code Standards
    Bars and shapes В52 GOST 13616-97, GOST 13617-97, GOST 13618-97, GOST 13619-97, GOST 13620-90, GOST 13621-90, GOST 13622-91, GOST 13623-90, GOST 13624-90, GOST 13737-90, GOST 13738-91, GOST 17575-90, GOST 17576-97, GOST 19657-84, GOST 29296-92, GOST 29303-92, GOST Р 50066-92, GOST Р 50067-92, GOST Р 50077-92
    Non-ferrous metals, including rare, and their alloys В51 GOST 14957-76, TU 1-4-015-80
    Bars В55 GOST 18351-73
    Tubes of non-ferrous metals and alloys В64 GOST 19441-74
    Sheets and strips В53 GOST 21990-76

    Chemical composition

    Standard Mn Si Ni Fe Cu Al Zn Mg Be
    GOST 14957-76 0.2-0.6 ≤0.01 ≤0.001 ≤0.005 ≤0.01 3.8-5 0.8-1.5 Rest ≤0.002
    Mg is the basis.
    According to GOST 14957-76 the mass fraction of other impurities is ≤ 0.10%. "Other impurities" include impurities whose permissible content limits are not indicated (≤), as well as impurities not included in the table, the content of which is not determined. Beryllium is not determined, but is introduced by calculation.

    Mechanical properties

    Section, mm sT|s0,2, MPa σU, MPa d HB, MPa
    Plate hot rolled according to GOST 21990-76 without heat treatment in the state of delivery (longitudinal samples)
    12-32 ≥137 ≥245 ≥8 -
    32-40 - ≥226 ≥6 -
    Extruded GOST 19657-84 without heat treatment in the state of delivery (in cross-section provided the cross-sectional area of the profile in cm2)
    5-12 ≥145 ≥255 ≥8 ≥42
    5 ≥155 ≥265 ≥9 ≥45
    Bars and rods, hot-pressed in the delivery condition without heat treatment according to GOST 18351-73 (longitudinal samples)
    160-200 - ≥245 ≥5 -
    8-160 ≥145 ≥255 ≥8 -
    Tubes extruded in the state of delivery according to GOST 19441-74 (samples)
    - - ≥225 ≥8 -

    Description mechanical marks

    Name Description
    sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
    σU Limit short-term strength
    d Elongation after rupture
    HB Brinell hardness number

    Physical characteristics

    Temperature Е, HPa r, kg/m3 l, W/(m · °C) R, Mr. · m
    20 42 1790 963 120

    A description of the physical symbols

    Name Description
    Е The normal elasticity modulus
    r Density
    l Coefficient of thermal conductivity
    С Specific heat