Designation
| Name |
The value |
| Designation GOST Cyrillic |
ХН33КВЮ |
| Designation GOST Latin |
XH33KBJu |
| Transliteration |
HN33KVYu |
| By chemical elements |
CrNi33CoВAl |
| Name |
The value |
| Designation GOST Cyrillic |
ВЖ145 |
| Designation GOST Latin |
BZh145 |
| Transliteration |
VG145 |
| By chemical elements |
ВFe145 |
| Name |
The value |
| Designation GOST Cyrillic |
ЭК102 |
| Designation GOST Latin |
EK102 |
| Transliteration |
EhK102 |
| By chemical elements |
- |
Description
Alloy ХН33КВЮ applied: manufacture of forgings intended for subsequent hot machining; forged rings; parts, used in aviation and other industries.
Standards
| Name |
Code |
Standards |
| Blanks. Of the workpiece. Slabs |
В31 |
TU 1-806-1068-99, TU 1-806-0907-2004 |
| Bars and shapes |
В32 |
TU 14-1-4568-89 |
| Processing of metals by pressure. Forgings |
В03 |
TU 14-1-4569-89 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Al |
W |
Co |
Nd |
| TU 14-1-4569-89 |
0.01-0.1 |
≤0.013 |
≤0.013 |
≤0.5 |
20-23 |
≤0.8 |
Rest |
≤3 |
0.3-0.7 |
13-16 |
26-30 |
≤0.1 |
Ni is the basis.
According to TU 14-1-4568-89 and TU 14-1-4569-89 the chemical composition is given for the alloy of the grades ХН33КВЮ-ВИ (ВЖ145-ВИ, ЭК102-ВИ), ХН33КВЮ-ИД (ВЖ145-ИД, ЭК102-ИД), ХН33КВЮ-ИШ (ВЖ145-ИШ, ЭК102-ISH). In the table of chemical composition in column Nd, the calculated content of neodymium or lanthanum is indicated. Neodymium or lanthanum are not determined by chemical analysis.
Mechanical properties
| Section, mm |
sT|s0,2, MPa |
σU, MPa |
d5, % |
y, % |
KCU, kJ/m2 |
| Ring rolled on the other 1-806-0907-2004. Quenching with 1180-1200 °With (extract 2.0 minutes per 1 mm cross section + 10 minutes), air cooling |
|
≥392 |
≥784 |
≥55 |
≥65 |
≥1960 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σU |
Limit short-term strength |
| d5 |
Elongation after rupture |
| y |
The relative narrowing |
| KCU |
Toughness |
Technological properties
| Name |
The value |
| Macrostructure and pollution |
The macrostructure of the alloy when tested for cross etched templeto should not have cracks, slag inclusions, voids and traces of shrinkage of the shell. |
| Particularities of production of goods |
Bars and rods, of alloy can be supplied under hot or under cold stamping, mechanical treatment, as specified in the order. On the surface of the bars under the hot stamping should not be captured, rolling rolled cracks, holes, sunsets and zakovou - local defects should be removed with gentle scraping. The depth of Stripping shall not exceed the tolerances for size, measured from face value. The ratio of the width of the Stripping depth should not be less than 6. No Stripping allowed some small risks and dents within half of the tolerance on size. On the surface of bars designed for cold mechanical processing is not allowed defects when their depth exceeds the tolerance size. Bars with a diameter or a side of a square of 80 mm or more are subject to ultrasonic inspection according to the method of the supplier. Rejection when UT is the presence of a defect, the amplitude of which is greater than or equal to the amplitude of the signal reflected from the flat end face of the control reflector with a diameter of 3.0 mm in the reference sample sensitivity located on the same (with a tolerance of -10 mm) or greater depth as the defect. |