Alloy 01Х18Н40М5ГБР (ЭП753Р)

  • Alloy 01X18H40M5G2TFRY (EP753U)
  • Alloy 01X18H40M5GB (EP753; ČS116)
  • Alloy 01X18H40M5GBR (EP753R)
  • Alloy 03KhN28MDT (EP516)
  • Alloy 06XHN28MDT (EI943)
  • Alloy 06XHN28MT (EI628)
  • Alloy Kh33TMMDU (EK63)
  • Alloy KhN30MDB (EK77)
  • Alloy CrN40B (EP337)
  • Alloy KhN40M5T2GYUBR (EK173)
  • Alloy CrN40MDB (EP937)
  • Alloy CrN40MDTU (EP543U)
  • Alloy CrN46B (EP350; 0Х20Н46B)

    • Designation

    Name The value
    Designation GOST Cyrillic 01Х18Н40М5ГБР
    Designation GOST Latin 01X18H40M5GBP
    Transliteration 01H18N40M5GBR
    By chemical elements 01Cr18Ni40Cu5GeBeHg
    Name The value
    Designation GOST Cyrillic ЭП753Р
    Designation GOST Latin EP753P
    Transliteration EhP753R
    By chemical elements -

    Description

    Alloy 01Х18Н40М5ГБР used: for the production of forged billets intended for production of high quality pipes applied in petrochemical industry, instrument manufacturing, specialty vehicles and nuclear power plants.

    Standards

    Name Code Standards
    Blanks. Of the workpiece. Slabs В31 TU 14-1-2097-77

    Chemical composition

    Standard C S P Mn Cr Si Ni Fe N V B Mo Nb Ce
    TU 14-1-2097-77 ≤0.01 ≤0.015 ≤0.01 1-2 17.5-19 ≤0.1 39-41 Rest ≤0.015 0.05-0.2 0.002-0.007 4.5-5 0.25-0.6 ≤0.05
    According to TU 14-1-2097-77, the chemical composition is presented for the alloy 01Х18Н40М5ГBR-ID (EP753R-ID), melted by the vacuum induction melting method followed by vacuum-arc remelting. In the alloy, deviations in the content of the elements are allowed: for carbon +0.0050%, for silicon +0.10%, for phosphorus +0.0050%, for molybdenum + 0.30%, for nitrogen + 0. 0050%, for boron +0.0030%. Cerium is introduced into the metal by calculation and chemical analysis is not determined. the residual impurity content should be (guaranteed by the manufacturer): cobalt ≤0.010%, copper ≤0.050%, arsenic ≤0.0050%, lead ≤ 0.00050%, cadmium ≤ 0.00050%, tin ≤0.0010%, zinc ≤ 0.0010%, antimony ≤0.0010%, bismuth ≤ 0.00050%, tantalum ≤0.0050%, titanium ≤0.050%. The deviation in the tantalum content is +0.0050%, titanium +0.050%.

    Mechanical properties

    Section, mm sT|s0,2, MPa σU, MPa d5, %
    The billet forged on the other 14-1-2097-77. Austenization at 1050-1080 °C, air cooling
    ≥196 ≥539 ≥45
    ≥127 ≥412 ≥47
    ≥98 ≥343 ≥45

    Description mechanical marks

    Name Description
    sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
    σU Limit short-term strength
    d5 Elongation after rupture

    Technological properties

    Name The value
    Macrostructure and pollution In the macrostructure of the workpiece in the state of delivery should be free of cracks, gas bubbles, subcortical bubbles, turns brown, inclusions, delaminations, traces of shrinkage of the shell, visible to the naked eye. Layer-by-layer crystallization and the square of the increased travelmasti are not rejection symptom. The evaluation of contamination of metal non-metallic inclusions. The norm of non-metallic inclusions by the maximum score: - sulphides ≤ 1.0 points; - nitrides and carbonitrides point ≤ 1.5 points; - nitrides and carbonitrides stroke ≤ 2.5 points. The total number of oxygen inclusions (granules and globules of oxide spinels, silicates and silicate glasses) shall not exceed: a) from 1 to 2 inclusive divisions of the ocular scale in 2 sections - 50 inclusions on 6 sections - 150 inclusions; b) from 2 to 5, inclusive divisions of the ocular scale in 2 sections - 1 for on, - for 6 sections - 3 inclusions; C) larger than 3 divisions of the ocular scale are not allowed.
    Particularities of production of goods Tubular billet on the other 14-1-2097-77 made in accordance with the terms of the supply 01-1874-62.
    Corrosion resistance Metal forged tube blank on the other 14-1-2097-77 must be able to withstand the test of susceptibility to intergranular attack according to the method of AM GOST 6032.