Powder material MV-50A

  • Steel PKr10-66 (Zhr10-66)
  • X18H15 steel
  • X13M2 steel
  • Powder material FMK-845
  • Powder material FMK-8
  • Powder material FMK-79
  • Powder material FMK-11
  • PKX25-75 steel (ZHX25-75)
  • Steel PKr70-72 (Zhr70-72)
  • Steel PKr70-69 (Zhr70-69)
  • Steel PKr50-70 (Zhr50-70)
  • Steel PKr10-76 (Zhr10-76)
  • Steel PKr10-72 (Zhr10-72)
  • PKr10-70 steel (Zhr10-70)
  • PK70D3-72 (Zh70D3-72) steel
  • Steel PK70D3-69 (Zh70D3-69)
  • Steel PK70D3-66 (Zh70D3-66)
  • Steel PK70-77 (Zh70-77)
  • Steel PK70-66 (Zh70-66)
  • Steel PK20Kh13M2-74 (Zh20Kh13M2-74)
  • PK10Kh18N15-67 (Zh10Kh18N15-70) steel
  • PK10Kh13M2D4-68 (Zh10Kh13M2D4-69)
  • Steel PK10K0,4-66 (Zh10K0,4-66)
  • Steel PK10-76 (Zh10-76)
  • Steel PK10-66 (Zh10-66)
  • Powder material MKV-50A

    • Designation

    Name The value
    Designation GOST Cyrillic МКВ-50А
    Designation GOST Latin MKB-50A
    Transliteration MKV-50A
    By chemical elements CuCoВ-50

    Description

    Powder material MV-50A is used: for the manufacture of parts designed to work in brakes, friction clutches and other friction devices.

    Note

    Sintered powder material based on iron.
    Parts is produced by powder metallurgy, by primechanie to steel base (frame) metal-ceramic friction material.

    Standards

    Name Code Standards
    Hard alloys, ceramic-metal products and metal powder В56 OST 1 90115-74

    Chemical composition

    Standard C S Si Fe Cu B
    OST 1 90115-74 8.5-11 0.6-1.2 3-4.3 Rest 9-11 3-4.3
    Fe is the basis.
    In addition to the components specified for OST 1 90115-74, asbestos is present in the cermet composition in the amount of 2.50-4.00%.

    Technological properties

    Name The value
    Particularities of production of goods Frames parts with metal-ceramic friction material brand MV-50A shall be made of steel groups 1 and 2 according to GOST 1616523; brand 20KH3MVF (ЭИ415) - according to GOST 20072, grade 30Х2ГСНВМА (ВЛ1-D) - on the other 14-1-711-73.
    Properties of the cermet Coefficient of friction - 0,330-0,404; the stability of the coefficient of friction is not less than 0.70; the wear Intensity of metal - not exceeding 12.0 ág/brake; the Intensity of wear of cast iron - not more than 9,0 MK/brake; Rockwell Hardness (ball diameter 1,588 mm at a load of 60 kg) of metal to the machining - 60-100. Properties when working together with metal stamps FMK-845: Coefficient of friction - 0,330-404; the stability of the coefficient of friction is not less than 0.70; the wear Intensity of metal - not more than 16.0 µg/brake; wear of FMK-845 - not exceeding 12.0 ág/brake; Rockwell Hardness (ball diameter 1,588 mm at a load of 60 kg) of metal to the machining - 65-100.